摘要
为更快速准确检测超低碳钢中的碳含量,分别对影响直读光谱仪分析超低碳钢含量的因素制样方式、氩气流量与压力进行了研究,确定了最优条件,并将分析结果与红外碳硫仪分析的结果进行了对比,结果表明直读光谱仪分析超低碳是一种具有分析速度快、准确度与精度高的方法。
The factors including sample making and argon gas flow and pressure are discussed that influence carbon content analysis in ultra-low carbon steel by direct-reading spectrometry to detect more accurately and quickly carbon content in ultra-low carbon steel.The results shows that the direct-reading spectrometry is satisfactory based on optimal analysis condition with high precision and accuracy by compared with infrared absorption method.
引文
[1]陈群芝.直读光谱法测定钢铁中常规元素结果准确性的探讨[J].理化检验,2012,48:23-29.
[2]邱永刚.超低碳钢冶炼碳、硫的控制工艺与实践[D].沈阳:东北大学,2010:1-2.
[3]左丽峰,连秀敏,刘博.直读光谱法分析低碳钢碳含量[A].第七届钢铁年会论文集[C],2009.
[4]李荟芳.光谱分析钢中超低碳的方法研究[J].辽宁科技学院学报,2015,17(1):6-7.
[5]王彬果,徐静,张建忠.对影响红外吸收法测定钢中超低碳含量稳定性的因素初探[J].冶金分析,2012,32:946-949.
[6]董金刚,贾宏,刘永勤,等.影响超低碳钢碳含量检测的几个因素[J].宝钢技术,2000(6):23-25.
[7]梁小丽,芦飞.提高直读光谱法测定不锈钢中超低碳的准确性[J].化学工程与技术,2014,4(5):72-77.
[8]杨琳,王明生,项秀智,等.试样表面碳对红外吸收常规法测定钢中超低碳影响的研究[J].冶金分析,2011,31(4):30-34.
[9]邢华宝,徐芬兰,胡正阳,等.钢铁中超低碳的分析[J].冶金分析,2001,24(2).24-25.
[10]高平,田甜.钢铁及合金化验技术[M].北京:化学工业出版社,2010:105-113.