硅酸钠改性聚乙烯醇耐水涂层的制备及研究
详细信息 查看官网全文
- 英文论文题名：Preparation and Property of Water Resistant Polyvinyl Alcohol Coating Modified by Sodium Silicate
- 论文作者：黄培林 ; 范天锋 ; 王德海
- 英文论文作者：Huang Peilin ; Fan Tianfeng ; Wang Dehai ; College of Chemical Engineering and Materials Science ; Zhejiang University of Technology
- 年：2016
- 作者机构：浙江工业大学材料科学与工程学院;
- 论文关键词：聚乙烯醇 ; 硅酸钠 ; 交联 ; 耐水性
- 英文论文关键词：polyvinyl alcohol ; sodium silicate ; cross-linked ; water resistance
- 会议召开时间：2016-11-14
- 会议录名称：2016年全国无机硅化物行业年会暨创新发展研讨会论文集
- 语种：中文
- 分类号：TQ630.1
- 学会代码：WJYG
- 会议名称：2016年全国无机硅化物行业年会暨创新发展研讨会
- 会议地点：中国河南郑州
- 主办单位：中国无机盐工业协会无机硅化物分会
- 学会名称：中国无机盐工业协会无机硅化物分会
- 页数：5
- 文件大小：330k
- 原文格式：O
- 会议级别：全国
摘要
通过硅酸钠在酸催化作用下与聚乙烯醇(PVA)反应制备有机-无机复合涂层,改善聚乙烯醇的耐水性。研究了酸种类、硅酸钠用量和热处理温度对复合涂层耐水性的影响。通过红外光谱(FITR)、X射线衍射(XRD)、差示扫描量热(DSC)、热重分析(TGA)对复合涂层结构进行了表征。结果表明:硅酸钠与PVA发生交联,PVA结晶度下降,热分解温度提高;随着硅酸钠用量增加,涂层耐水性先提高后下降;选用磷酸作为催化剂,热处理温度在120~140℃较为合适,复合涂层具有较好的耐水性。
An organic-inorganic coating was prepared by the reaction of sodium silicate with polyvinyl alcohol(PVA) at the presence of acidic catalyst so as to improve the water resistance.The effects of catalyst type,sodium silicate content and heat treatment temperature on the water resistance of the composite coating were studied.The structures of the coating films were characterized by infrared spectroscopy(FI- TR),X-ray diffraction(XRD),differential scanning calorimetry(DSC) and thermal gravimetric analyzer(TGA).The results showed that sodium silicate and PVA were cross-linked,the crystallinity of PVA decreased,thermal decomposition temperature increased.Widi the increase of sodium silicate,the water resistance of the coating increased first and then decreased.In addition,the phosphoric acid was used as a catalyst,the heat treatment temperature ranged preferably from 120 to 140 ℃,enabling the composite coating to show an improved water resistance.
An organic-inorganic coating was prepared by the reaction of sodium silicate with polyvinyl alcohol(PVA) at the presence of acidic catalyst so as to improve the water resistance.The effects of catalyst type,sodium silicate content and heat treatment temperature on the water resistance of the composite coating were studied.The structures of the coating films were characterized by infrared spectroscopy(FI- TR),X-ray diffraction(XRD),differential scanning calorimetry(DSC) and thermal gravimetric analyzer(TGA).The results showed that sodium silicate and PVA were cross-linked,the crystallinity of PVA decreased,thermal decomposition temperature increased.Widi the increase of sodium silicate,the water resistance of the coating increased first and then decreased.In addition,the phosphoric acid was used as a catalyst,the heat treatment temperature ranged preferably from 120 to 140 ℃,enabling the composite coating to show an improved water resistance.