A simple and efficient procedure has been developed to fabricate Zn O nanofibers by electrospinning and subsequent calcination. With the hydrothermal method the Ag nanoparticles(Ag Nps) were decorated on the surface of the Zn O nanofibers. Structure and component of Ag/Zn O samples were characterized by XRD, XPS, EDX and DRS. Morphology was studied by SEM and TEM, the images reveal that the diameters of Zn O nanofibers are from 80-330 nm and the Ag Nps are from 5-100 nm attached to the Zn O nanofibers form the heterostructure. The photocatalysis properties were verified by degradation of methyl orange dye and the Ag/Zn O samples showed efficient photocatalytic activity for the degradation of a simulation of pollutants.
A simple and efficient procedure has been developed to fabricate Zn O nanofibers by electrospinning and subsequent calcination. With the hydrothermal method the Ag nanoparticles(Ag Nps) were decorated on the surface of the Zn O nanofibers. Structure and component of Ag/Zn O samples were characterized by XRD, XPS, EDX and DRS. Morphology was studied by SEM and TEM, the images reveal that the diameters of Zn O nanofibers are from 80-330 nm and the Ag Nps are from 5-100 nm attached to the Zn O nanofibers form the heterostructure. The photocatalysis properties were verified by degradation of methyl orange dye and the Ag/Zn O samples showed efficient photocatalytic activity for the degradation of a simulation of pollutants.
引文