飞机座舱有机玻璃材料疲劳性能分析
|
摘要
有机玻璃材料由于具有较好的透光性和足够的结构强度而广泛应用于飞机座舱盖、风挡等结构中。有机玻璃结构的疲劳性能是一个重要指标,飞机座舱盖的疲劳定寿工作是飞机结构疲劳定寿的重要内容之一。
本文首先回顾了有机玻璃材料的疲劳行为,综述了材料的蠕变模型及与松弛模型之间的关系,介绍了有机玻璃材料疲劳寿命估算方法,设计了蠕变试验及试验装置,完成了 YB-3 有机玻璃试件的单轴拉伸蠕变试验与疲劳试验,给出了试验结果,分析了试验条件对结果产生的影响。基于损伤力学,提出了一个适合于 YB-3 有机玻璃材料的蠕变损伤的修正模型,结合蠕变试验结果,成功描述了蠕变行为,预测了蠕变断裂时间;并结合疲劳试验结果,分析得到蠕变/疲劳损伤演化模型,模型的预测结果与试验结果吻合较好。
本文的算例表明,所提出的修正模型能够成功分离出试验结果中的蠕变损伤和纯疲劳损伤。
Polymethyl Methacrylate(PMMA) has been widely used in the wind shield of aircraft because of its excellent transparency and strength. The fatigue behaviour of PMMA is very important for the aircraft windshield structure.
The commonly used creep models, relaxation models and the relationships between creep and relaxation of PMMA are reviewed in the present thesis. The prediction approaches of fatigue life of PMMA structures are discussed. A simple test device for creep experiment was designed. Axial creep experiment and fatigue experiment of YB-3 PMMA had been carried out. Based on continuum damage mechanics, a modified model to describe the creep damage of YB-3 is developed. Creep experiment data proved that this model can explain creep behavior better and predict creep fracture time of YB-3 more accurately. A creep and fatigue damage model has been presented to explain fatigue test results. There is excellent consistency between the predicted and experiment data.
本文首先回顾了有机玻璃材料的疲劳行为,综述了材料的蠕变模型及与松弛模型之间的关系,介绍了有机玻璃材料疲劳寿命估算方法,设计了蠕变试验及试验装置,完成了 YB-3 有机玻璃试件的单轴拉伸蠕变试验与疲劳试验,给出了试验结果,分析了试验条件对结果产生的影响。基于损伤力学,提出了一个适合于 YB-3 有机玻璃材料的蠕变损伤的修正模型,结合蠕变试验结果,成功描述了蠕变行为,预测了蠕变断裂时间;并结合疲劳试验结果,分析得到蠕变/疲劳损伤演化模型,模型的预测结果与试验结果吻合较好。
本文的算例表明,所提出的修正模型能够成功分离出试验结果中的蠕变损伤和纯疲劳损伤。
Polymethyl Methacrylate(PMMA) has been widely used in the wind shield of aircraft because of its excellent transparency and strength. The fatigue behaviour of PMMA is very important for the aircraft windshield structure.
The commonly used creep models, relaxation models and the relationships between creep and relaxation of PMMA are reviewed in the present thesis. The prediction approaches of fatigue life of PMMA structures are discussed. A simple test device for creep experiment was designed. Axial creep experiment and fatigue experiment of YB-3 PMMA had been carried out. Based on continuum damage mechanics, a modified model to describe the creep damage of YB-3 is developed. Creep experiment data proved that this model can explain creep behavior better and predict creep fracture time of YB-3 more accurately. A creep and fatigue damage model has been presented to explain fatigue test results. There is excellent consistency between the predicted and experiment data.
引文
[1] 高镇同,有机玻璃疲劳和断口图谱[M],北京:科学出版社,1987.
[2] 航空工业部门科学技术委员会,飞机结构疲劳定寿文集:1-3 集[C],航空工业部科学技术委员会,1987.
[3] 邸祥发,飞机座舱透明件疲劳寿命分析中几个修正系数的确定[J],飞机设计,1994(3):49~60.
[4] 徐世清,YB-3 座舱盖玻璃开裂失效分析[J],航空工业技术,1995(4):33~35.
[5] 任瑞,靳耿栓,郭秀梅,舱盖玻璃裂纹原因分析及工艺改进[J],技术改造·技术革新.
[6] 邸祥发,袁贵民,飞机座舱盖透明件加温-加载谱的制定[J],飞机设计,1997(4):20~24.
[7] 邸祥发,王佳莹,透明件强度设计应考虑材料的综合性能[J],飞机设计,2002(3):64~66.
[8] 谢洪钧,教 8 飞机座舱盖的设计制造与骨架工艺分析[J],洪都科技,1991(1):1~8.
[9] 吴建辉,K8 飞机座舱盖有机玻璃破裂原因分析[J],洪都科技,1999:25~34.
[10] 许凤和,邸祥发,过梅丽,航空非金属件失效分析[M],北京:科学出版社,1993.
[11] 李之达,周衍领,张嵘峰,蠕变条件下 PMMA 银纹损伤的实验研究[J],湘潭大学自然科学学报,2003,25(4):38~40.
[12] 颜鸣皋,工程材料实用手册:第 5 册[S],北京:中国标准出版社,1988:204~214.
[13] 刘立厚,黄耀祥,蔡宗熙,材料松弛与蠕变函数的相互转换[J],河北建筑科技学院学报,1998,15(2):6~15.
[14] 郭大智,任瑞波. 层状粘弹性体系力学[M]. 哈尔滨:哈尔滨工业大学出版社,2001.
[15] 李漪. 拉普拉斯变换在聚合物粘弹性理论中的应用[J]. 上海交通大学学报,1996,30(5):141~145.
[16] 魏培君,粘弹性力学的对应原理及其数值反演方法[J],力学进展,1999,29(3):317~330
[17] Christensen. R. M. Theory of Viscoelasticity, an lntroduction, 2 nd Ed., [S.l.]:Academic Press lnc.,1982,122~156
[18] 赵伯华,松弛与蠕变力学特性转换关系的研究[J],实验力学,1995,10(2):140~144
[19] 张为民,松弛模量与蠕变柔量的实用表达式[J],湘潭大学自然科学学报,1999,21(3):26~28
[20] 刘朝辉,张为民,含分数阶导数的粘弹性固体模型及其应用[J],株洲工学院学报,2002,16(4):23~25
[21] Chien L. S, Tzeng J T. Thermal viscoelastic analysis for thick-walled composite cylinders[J]. Journal of Composite Materials, 1995,29:525~548
[22] Ferry J. D. Viscelastic Properties of Polymers, 3 rd ,New York:Wiley, 1980,56~129
[23] 刘军虎,王铮,由应力松弛试验数据确定松弛模量和蠕变柔量[J],固体火箭技术,1995,18(3):73~78
[24] 郑立春,姚卫星,疲劳裂纹形成寿命预测方法综述[J],力学与实践,1996(4):9~14
[25] 郑立春,姚卫星,张云阁,预测疲劳裂纹形成寿命的局部应力应变方法之评述[J],强度与环境,1996(2):12~18
[26] 吴富民,结构疲劳强度[M],西安:西北工业大学出版社,1985
[27] 姚卫星,结构疲劳寿命分析[M],北京:国防工业出版社,2003
[28] Yao W. X. Stress Field Intensity Approach for Prediction Fatigue Life[J]. Internationnal Journal of Fatigue,1993,15(3):243-245
[29] 许凤和,李晓骏,陈新文等,飞机座舱透明材料大气老化与使用老化当量关系的研究[J],航空学报,2001,22(1):91~93
[30] 张志林,姚卫星,飞机座舱有机玻璃结构疲劳寿命估算的局部应力法[J],南京航空航天大学学报,2004,36(3):298~301
[31] 穆霞英,蠕变力学[M],西安:西安交通大学出版社,1989
[32] 许凤和,高分子材料力学试验[M],科学出版社,1988
[33] 马德柱等,高聚物的结构与性能[M],科学出版社,1995
[34] 高俊刚,李源勋,高分子材料[M],化学工业出版社,2002
[35] Lemaitre J. A Continuous Damage Mechanics Model for Ductile Fracture[J]. J. of Eng. Materials and Technology, 1985, 107(1):83~89
[36] Lemaitre J., Plumtree A. JEMT.T rams ASME V ol.101,1979
[37] Lemaitre J., Local Approach of Fracture[J].Engineering Fracture Mechanics, 1986:25:523~537
[38] Lemaitre J. Proc. SMIRT. 7, San Francisco, 1983
[39] J. Lemaitre. 损伤力学教程[M],北京:科学出版社,1996
[40] Lemaitre J and Chaboche J. Aspect phenomenologique de la rupture par endommagement[J]. J. Mecanique Appliquee, 1978, 2(3):317~365
[41] Kachanov L. M. Time of the Rupture Process under Creep Conditions[J]. lzv. Akad. Nauk. SSSR. Old. Tekh. Nauk.1958:8:26~31
[42] Kachanov L. M. Introduction to Continuum Damage Mechanis[M]. Martinus Nijhoff Publishers, 1986
[43] Качанов Л М. О Времени разрущения в условиях пользучести[J], Изв.АН.СССР, ОТН.,1958,8,23~31
[44] 吴鸿遥,损伤力学[M],北京:国防工业出版社,1990
[45] J L Chaboche, Continuum Damage Mechanics: Part Ⅱ—Damage Growth, Crack lnitiation, and Crack Growth[J]. Journal of Applied Mechanics, 1988, Vol.55:65~72
[46] 李兆霞,损伤力学及其应用[M],北京:科学出版社,2002
[47] 余天庆,钱济成,损伤理论及其应用[M],北京:国防工业出版社
[48] L.M.卡恰诺夫,连续介质损伤力学引论[M],哈尔滨:哈尔滨工业大学出版社,1989
[49] 余寿文,冯西桥,损伤力学[M],北京:清华大学出版社,1997
[50] 王军,损伤力学的理论与应用[M],北京:科学出版社,1997
[51] 楼志文,损伤力学基础[M],西安:西安交通大学出版社,1991
[52] 沈为,彭立华,疲劳损伤演变方程与寿命估算—连续损伤力学的应用[J],机械强度,1994,16(2):52~57
[53] 鹿晓阳,连续损伤力学的基本理论方法及工程应用[J],山东建筑工程学院学报,1994,9(2):1~7
[54] Krajcinovic D, Lemaitre I. Continuum Damage Mechanics Theory and Application[J]. CISM Courses and Lectures.1987:295
[55] J. C. Arnold, V. E. White. Predictive Models for the Creep behaviour of PMMA[J], Materials Science and Engineering A197(1995):251~260
[56] 罗成利,姚卫星,有机玻璃结构疲劳寿命预测的损伤力学方法[J],机械强度,2004,26(S):087~088 (EI 04498707076)
[57] 周道祥,孙训方,结构元件蠕变与疲劳寿命估算方法研究进展[J], 安徽建筑工业学院学报(自然科学版),1999,7(1):1~8
[58] 孙训方,蠕变与疲劳共同作用下结构元件的寿命估算[J],成都:西安交通大学出版社,1986
[59] 孙训方,周道祥,蠕变与疲劳作用下结构元件寿命估算[J],安徽建筑工业学院学报(自然科学版),1998,6(4):1~11
[60] M. Miyahara. K. Tokimasa. Life Prediction of High Temperature Structural Component by Strain Range Partitioning[J]. Acta Metallurgica Sinica.1999,Vol.12 No.1 pp 43-50
[61] N. Wang, B. S. Zhou, Z. D. Wang and D. D. Wu. A Damage Model of Life Prediction Under Creep-Fatigue Interaction[J]. Acta Metallurgica Sinica. 1999, Vol. 12 No. 1 pp 28-32
[62] 汤晓英,10CrMo910 钢的蠕变损伤分析[J],材料工程,2002,19(5):9~11
[63] 汤晓英,10CrMo910 钢的蠕变、疲劳及其交互作用的损伤分析[D],上海:华东理工大学,2000
[64] 郝红伟,施光凯,Origin 6.0 实用教程[M],北京:中国电力出版社,2000
[65] J. L. Chaboche, Lifetime Predictions and Cumulative Damage under High-Temperature Conditions[J]. Low-Cycle Fatigue and Life Prediction,1982:81~102
[66] Krajcinovic D., Sumarac D., Continuum damage mechanics[M], J. Lemaitre,1987:135~194
[67] Berstein H L., Low-Cycle Fatigue and Life Predicion[J], ASME, STP 770,1982:105
[68] Batte A D., Creep-Fatigue Life Predictions, Fatigue at High Temperature[M], New York: Applied Science Publishers, 1983, 365
[69] Y. C. Xiao, S, Li and Z. Gao, A Continuum Damage Mechanics Model for High Cycle Fatigue[J], Int, J., Fatigue Vol, 20, No, 7, pp, 503–508, 1998
[70] J. J. Martinez-Vega, H, Trumel, J. L. Gacougnolle, Plastic deformation and physical ageing in PMMA[J], Polymer 43(2002):4979~4981
[2] 航空工业部门科学技术委员会,飞机结构疲劳定寿文集:1-3 集[C],航空工业部科学技术委员会,1987.
[3] 邸祥发,飞机座舱透明件疲劳寿命分析中几个修正系数的确定[J],飞机设计,1994(3):49~60.
[4] 徐世清,YB-3 座舱盖玻璃开裂失效分析[J],航空工业技术,1995(4):33~35.
[5] 任瑞,靳耿栓,郭秀梅,舱盖玻璃裂纹原因分析及工艺改进[J],技术改造·技术革新.
[6] 邸祥发,袁贵民,飞机座舱盖透明件加温-加载谱的制定[J],飞机设计,1997(4):20~24.
[7] 邸祥发,王佳莹,透明件强度设计应考虑材料的综合性能[J],飞机设计,2002(3):64~66.
[8] 谢洪钧,教 8 飞机座舱盖的设计制造与骨架工艺分析[J],洪都科技,1991(1):1~8.
[9] 吴建辉,K8 飞机座舱盖有机玻璃破裂原因分析[J],洪都科技,1999:25~34.
[10] 许凤和,邸祥发,过梅丽,航空非金属件失效分析[M],北京:科学出版社,1993.
[11] 李之达,周衍领,张嵘峰,蠕变条件下 PMMA 银纹损伤的实验研究[J],湘潭大学自然科学学报,2003,25(4):38~40.
[12] 颜鸣皋,工程材料实用手册:第 5 册[S],北京:中国标准出版社,1988:204~214.
[13] 刘立厚,黄耀祥,蔡宗熙,材料松弛与蠕变函数的相互转换[J],河北建筑科技学院学报,1998,15(2):6~15.
[14] 郭大智,任瑞波. 层状粘弹性体系力学[M]. 哈尔滨:哈尔滨工业大学出版社,2001.
[15] 李漪. 拉普拉斯变换在聚合物粘弹性理论中的应用[J]. 上海交通大学学报,1996,30(5):141~145.
[16] 魏培君,粘弹性力学的对应原理及其数值反演方法[J],力学进展,1999,29(3):317~330
[17] Christensen. R. M. Theory of Viscoelasticity, an lntroduction, 2 nd Ed., [S.l.]:Academic Press lnc.,1982,122~156
[18] 赵伯华,松弛与蠕变力学特性转换关系的研究[J],实验力学,1995,10(2):140~144
[19] 张为民,松弛模量与蠕变柔量的实用表达式[J],湘潭大学自然科学学报,1999,21(3):26~28
[20] 刘朝辉,张为民,含分数阶导数的粘弹性固体模型及其应用[J],株洲工学院学报,2002,16(4):23~25
[21] Chien L. S, Tzeng J T. Thermal viscoelastic analysis for thick-walled composite cylinders[J]. Journal of Composite Materials, 1995,29:525~548
[22] Ferry J. D. Viscelastic Properties of Polymers, 3 rd ,New York:Wiley, 1980,56~129
[23] 刘军虎,王铮,由应力松弛试验数据确定松弛模量和蠕变柔量[J],固体火箭技术,1995,18(3):73~78
[24] 郑立春,姚卫星,疲劳裂纹形成寿命预测方法综述[J],力学与实践,1996(4):9~14
[25] 郑立春,姚卫星,张云阁,预测疲劳裂纹形成寿命的局部应力应变方法之评述[J],强度与环境,1996(2):12~18
[26] 吴富民,结构疲劳强度[M],西安:西北工业大学出版社,1985
[27] 姚卫星,结构疲劳寿命分析[M],北京:国防工业出版社,2003
[28] Yao W. X. Stress Field Intensity Approach for Prediction Fatigue Life[J]. Internationnal Journal of Fatigue,1993,15(3):243-245
[29] 许凤和,李晓骏,陈新文等,飞机座舱透明材料大气老化与使用老化当量关系的研究[J],航空学报,2001,22(1):91~93
[30] 张志林,姚卫星,飞机座舱有机玻璃结构疲劳寿命估算的局部应力法[J],南京航空航天大学学报,2004,36(3):298~301
[31] 穆霞英,蠕变力学[M],西安:西安交通大学出版社,1989
[32] 许凤和,高分子材料力学试验[M],科学出版社,1988
[33] 马德柱等,高聚物的结构与性能[M],科学出版社,1995
[34] 高俊刚,李源勋,高分子材料[M],化学工业出版社,2002
[35] Lemaitre J. A Continuous Damage Mechanics Model for Ductile Fracture[J]. J. of Eng. Materials and Technology, 1985, 107(1):83~89
[36] Lemaitre J., Plumtree A. JEMT.T rams ASME V ol.101,1979
[37] Lemaitre J., Local Approach of Fracture[J].Engineering Fracture Mechanics, 1986:25:523~537
[38] Lemaitre J. Proc. SMIRT. 7, San Francisco, 1983
[39] J. Lemaitre. 损伤力学教程[M],北京:科学出版社,1996
[40] Lemaitre J and Chaboche J. Aspect phenomenologique de la rupture par endommagement[J]. J. Mecanique Appliquee, 1978, 2(3):317~365
[41] Kachanov L. M. Time of the Rupture Process under Creep Conditions[J]. lzv. Akad. Nauk. SSSR. Old. Tekh. Nauk.1958:8:26~31
[42] Kachanov L. M. Introduction to Continuum Damage Mechanis[M]. Martinus Nijhoff Publishers, 1986
[43] Качанов Л М. О Времени разрущения в условиях пользучести[J], Изв.АН.СССР, ОТН.,1958,8,23~31
[44] 吴鸿遥,损伤力学[M],北京:国防工业出版社,1990
[45] J L Chaboche, Continuum Damage Mechanics: Part Ⅱ—Damage Growth, Crack lnitiation, and Crack Growth[J]. Journal of Applied Mechanics, 1988, Vol.55:65~72
[46] 李兆霞,损伤力学及其应用[M],北京:科学出版社,2002
[47] 余天庆,钱济成,损伤理论及其应用[M],北京:国防工业出版社
[48] L.M.卡恰诺夫,连续介质损伤力学引论[M],哈尔滨:哈尔滨工业大学出版社,1989
[49] 余寿文,冯西桥,损伤力学[M],北京:清华大学出版社,1997
[50] 王军,损伤力学的理论与应用[M],北京:科学出版社,1997
[51] 楼志文,损伤力学基础[M],西安:西安交通大学出版社,1991
[52] 沈为,彭立华,疲劳损伤演变方程与寿命估算—连续损伤力学的应用[J],机械强度,1994,16(2):52~57
[53] 鹿晓阳,连续损伤力学的基本理论方法及工程应用[J],山东建筑工程学院学报,1994,9(2):1~7
[54] Krajcinovic D, Lemaitre I. Continuum Damage Mechanics Theory and Application[J]. CISM Courses and Lectures.1987:295
[55] J. C. Arnold, V. E. White. Predictive Models for the Creep behaviour of PMMA[J], Materials Science and Engineering A197(1995):251~260
[56] 罗成利,姚卫星,有机玻璃结构疲劳寿命预测的损伤力学方法[J],机械强度,2004,26(S):087~088 (EI 04498707076)
[57] 周道祥,孙训方,结构元件蠕变与疲劳寿命估算方法研究进展[J], 安徽建筑工业学院学报(自然科学版),1999,7(1):1~8
[58] 孙训方,蠕变与疲劳共同作用下结构元件的寿命估算[J],成都:西安交通大学出版社,1986
[59] 孙训方,周道祥,蠕变与疲劳作用下结构元件寿命估算[J],安徽建筑工业学院学报(自然科学版),1998,6(4):1~11
[60] M. Miyahara. K. Tokimasa. Life Prediction of High Temperature Structural Component by Strain Range Partitioning[J]. Acta Metallurgica Sinica.1999,Vol.12 No.1 pp 43-50
[61] N. Wang, B. S. Zhou, Z. D. Wang and D. D. Wu. A Damage Model of Life Prediction Under Creep-Fatigue Interaction[J]. Acta Metallurgica Sinica. 1999, Vol. 12 No. 1 pp 28-32
[62] 汤晓英,10CrMo910 钢的蠕变损伤分析[J],材料工程,2002,19(5):9~11
[63] 汤晓英,10CrMo910 钢的蠕变、疲劳及其交互作用的损伤分析[D],上海:华东理工大学,2000
[64] 郝红伟,施光凯,Origin 6.0 实用教程[M],北京:中国电力出版社,2000
[65] J. L. Chaboche, Lifetime Predictions and Cumulative Damage under High-Temperature Conditions[J]. Low-Cycle Fatigue and Life Prediction,1982:81~102
[66] Krajcinovic D., Sumarac D., Continuum damage mechanics[M], J. Lemaitre,1987:135~194
[67] Berstein H L., Low-Cycle Fatigue and Life Predicion[J], ASME, STP 770,1982:105
[68] Batte A D., Creep-Fatigue Life Predictions, Fatigue at High Temperature[M], New York: Applied Science Publishers, 1983, 365
[69] Y. C. Xiao, S, Li and Z. Gao, A Continuum Damage Mechanics Model for High Cycle Fatigue[J], Int, J., Fatigue Vol, 20, No, 7, pp, 503–508, 1998
[70] J. J. Martinez-Vega, H, Trumel, J. L. Gacougnolle, Plastic deformation and physical ageing in PMMA[J], Polymer 43(2002):4979~4981