摘要
本文以中铁一局集团办公大楼筏板大体积混凝土温度收缩裂缝控制为研究对象，针对筏板大体积混凝土产生裂缝的主要原因是温度应力和温度变形这一特点，重点研究筏板大体积混凝土内部最高温度和表面温度理论计算结果和实际测温结果的差异，探讨防止筏板大体积混凝土出现温度收缩裂缝的施工技术，提供切实可行的实践经验。
首先，本文以现有理论为基础，针对筏板大体积混凝土产生裂缝的四个原因，从混凝土配合比设计、内部温升及温度应力三个方面进行计算分析，重点对筏板大体积混凝土温度收缩抗裂度验算进行详细论述。
其次，根据筏板大体积混凝土配合比设计、内部温升及温度应力的计算结果，设计筏板大体积混凝土施工方案，提出了本工程为防止大体积混凝土温度收缩裂缝所采取的九项技术措施。
第三，将筏板大体积混凝土实际测温结果同理论计算结果进行对比分析，得出了本文的结论，供类似工程参考。
最后，本文以中铁一局集团办公大楼筏板大体积混凝土施工为实例，从混凝土配合比的确定、温度应力及保温材料厚度计算、混凝土的浇筑、混凝土内部实际温度的监测和后期养护等方面对本文阐述的筏板大体积混凝土施工方案进行了具体实施。工程实践表明，此施工方案中所采取的防止筏板大体积混凝土温度裂缝的九项技术措施是行之有效的。
This article take a iron game of CRFG office block raft board mass concrete temperature contraction crack control as object of study, concrete has the crack primary cause in view of the raft board great volume is the temperature stress and thermal distortion this characteristic, the key research raft board mass concrete interior maximum temperature and the surface temperature theoretical calculation result and the actual temperature measurement result difference, the discussion prevented the raft board mass concrete appears the temperature contraction crack the construction technology, provides the practical and feasible experience.
First, this article take the existing theory as a foundation, roughly accumulates four reasons in view of the raft board which the coagulation local product seams, from the proportioning of concrete design, internal temperature rise and the temperature stress three aspects carries on the computation analysis, key carries on the detailed elaboration to the raft board mass concrete temperature contraction cleavage resistance checking calculation.
Next, according to the raft board mass concrete mixture ratio design, internal temperature rise and the temperature stress computed result, designs the raft board mass concrete construction plan, proposed this project for prevented the mass concrete temperature contraction crack adopts nine technical measures.
Third, carries on the raft board great volume concrete actual temperature measurement result same theoretical calculation result the contrast analysis, has drawn this article conclusion, for similar project reference.
Finally, this article take a iron game of CRFG office block raft board mass concrete construction as an example, from the proportioning of concrete determination, the temperature stress and the thermal insulation material thickness computation, the concrete construction, the concrete internal actual temperature monitor and the later period maintained and so on the aspects the raft board mass concrete construction plan which elaborated to this article to carry on the concrete implementation. The project practice indicated, in this construction plan adopts prevented the raft board mass concrete temperature crack nine technical measure is effective.
首先，本文以现有理论为基础，针对筏板大体积混凝土产生裂缝的四个原因，从混凝土配合比设计、内部温升及温度应力三个方面进行计算分析，重点对筏板大体积混凝土温度收缩抗裂度验算进行详细论述。
其次，根据筏板大体积混凝土配合比设计、内部温升及温度应力的计算结果，设计筏板大体积混凝土施工方案，提出了本工程为防止大体积混凝土温度收缩裂缝所采取的九项技术措施。
第三，将筏板大体积混凝土实际测温结果同理论计算结果进行对比分析，得出了本文的结论，供类似工程参考。
最后，本文以中铁一局集团办公大楼筏板大体积混凝土施工为实例，从混凝土配合比的确定、温度应力及保温材料厚度计算、混凝土的浇筑、混凝土内部实际温度的监测和后期养护等方面对本文阐述的筏板大体积混凝土施工方案进行了具体实施。工程实践表明，此施工方案中所采取的防止筏板大体积混凝土温度裂缝的九项技术措施是行之有效的。
This article take a iron game of CRFG office block raft board mass concrete temperature contraction crack control as object of study, concrete has the crack primary cause in view of the raft board great volume is the temperature stress and thermal distortion this characteristic, the key research raft board mass concrete interior maximum temperature and the surface temperature theoretical calculation result and the actual temperature measurement result difference, the discussion prevented the raft board mass concrete appears the temperature contraction crack the construction technology, provides the practical and feasible experience.
First, this article take the existing theory as a foundation, roughly accumulates four reasons in view of the raft board which the coagulation local product seams, from the proportioning of concrete design, internal temperature rise and the temperature stress three aspects carries on the computation analysis, key carries on the detailed elaboration to the raft board mass concrete temperature contraction cleavage resistance checking calculation.
Next, according to the raft board mass concrete mixture ratio design, internal temperature rise and the temperature stress computed result, designs the raft board mass concrete construction plan, proposed this project for prevented the mass concrete temperature contraction crack adopts nine technical measures.
Third, carries on the raft board great volume concrete actual temperature measurement result same theoretical calculation result the contrast analysis, has drawn this article conclusion, for similar project reference.
Finally, this article take a iron game of CRFG office block raft board mass concrete construction as an example, from the proportioning of concrete determination, the temperature stress and the thermal insulation material thickness computation, the concrete construction, the concrete internal actual temperature monitor and the later period maintained and so on the aspects the raft board mass concrete construction plan which elaborated to this article to carry on the concrete implementation. The project practice indicated, in this construction plan adopts prevented the raft board mass concrete temperature crack nine technical measure is effective.
引文
1 江正荣．实用高层建筑施工手册．中国建筑工业出版社．2003年：281，284-292，294-300
2 混凝土结构结构工程施工质量验收规范．中国建筑工业出版社．2002年
3 何文杰．取消后浇缝的工程设计．四川建筑科学研究．1999年第2期：22
4 普通混凝土配合比设计规程(JGJ55-2000)．中国建筑工业出版社．2001年：4-11
5 杨嗣信．高层建筑施工手册．2．中国建筑工业出版社．2001年：488-491
6 王铁梦．工程结构裂缝控制．中国建筑工业出版社．1997年
7 混凝土结构设计规范(GB50010-2002)．中国建筑工业出版社．2002年．13
8 王国秉．防止水工混凝土裂缝的措施和修补方法．山西水利科技．2001年第1期．31
9 赵志缙．高层建筑施工手册．同济大学出版社．1991年．379-430
10 舒良成．“新世界商务中心”大体积混凝土裂缝控制措施．国外建材科技．2004年第3期．77-79
11 赵碧华、刘为民、黄耀武．大体积粉煤灰混凝土早期裂缝的施工控制．施工技术．2005年第34卷．23-24
12 江志强．大体积混凝土测温及温度裂缝控制实践．福建建设科技．2006年第4期．83-87
13 彭立海、阎士勤、张春生、翟建．大体积混凝土温控与防裂．黄河水利出版社．2005年
14 张雄．混凝土结构裂缝防治技术．化学工业出版社．2007年
15 李达、暴育红．大体积混凝土的温差裂缝控制及热工计算．混凝土．2006年第3期．88-90
16 孙柏峰．大体积混凝土浇筑后裂缝控制及降温保温工艺探讨．安徽建筑．2004年第2期．82-83
17 齐有章．大体积混凝土结构裂缝控制探讨．铁道建筑．2006年3期．97-98
18 秦春芳．建筑施工安全技术手册．中国建筑工业出版社．1991年
19 金信．建筑企业管理学．2．中国建筑工业出版社．2004年
20 成行、孔卓．大体积混凝土裂缝产生原因及控制措施．低温建筑技术．2005年第5期．112-113
21 叶琳昌、沈义．大体积混施工．中国建筑工业出版社．1986年
22 吴中伟、廉慧珍．高性能混凝土．中国铁道出版社．1999年
23 王刚、肖小玲．大体积混凝土裂缝的原因及控制．四川建筑．2004年第4期．102-103
24 白洪江．大体积混凝土裂缝控制措施．铁道建筑技术．2006年1期．65-67
25 陈金德．筏基大体积混凝土的裂缝控制．山西建筑．2006年9期．122-123
26 刘德慧．西宁某高层建筑基础大体积混凝土的温度裂缝控制技术．青海大学学报．第24卷第3期．12-14页
27 李苑．大体积混凝土温度裂缝控制．建筑技术．第37卷第4期．290-292
28 薛礼兵、王旭峰．大体积混凝土温度裂缝在实际工程中的控制技术．结构工程师．第22卷第4期．86-93
29 卞国祥、孙谨、于军．深圳会议展览中心大体积混凝土施工及长墙的裂缝控制．建筑技术．第35卷第4期．274-276
30 吴培明．混凝土结构上册(上册)．武汉工业大学出版社．2001年
31 李亚东．新编土木工程专业英语．西南交通大学出版社．2000年
2 混凝土结构结构工程施工质量验收规范．中国建筑工业出版社．2002年
3 何文杰．取消后浇缝的工程设计．四川建筑科学研究．1999年第2期：22
4 普通混凝土配合比设计规程(JGJ55-2000)．中国建筑工业出版社．2001年：4-11
5 杨嗣信．高层建筑施工手册．2．中国建筑工业出版社．2001年：488-491
6 王铁梦．工程结构裂缝控制．中国建筑工业出版社．1997年
7 混凝土结构设计规范(GB50010-2002)．中国建筑工业出版社．2002年．13
8 王国秉．防止水工混凝土裂缝的措施和修补方法．山西水利科技．2001年第1期．31
9 赵志缙．高层建筑施工手册．同济大学出版社．1991年．379-430
10 舒良成．“新世界商务中心”大体积混凝土裂缝控制措施．国外建材科技．2004年第3期．77-79
11 赵碧华、刘为民、黄耀武．大体积粉煤灰混凝土早期裂缝的施工控制．施工技术．2005年第34卷．23-24
12 江志强．大体积混凝土测温及温度裂缝控制实践．福建建设科技．2006年第4期．83-87
13 彭立海、阎士勤、张春生、翟建．大体积混凝土温控与防裂．黄河水利出版社．2005年
14 张雄．混凝土结构裂缝防治技术．化学工业出版社．2007年
15 李达、暴育红．大体积混凝土的温差裂缝控制及热工计算．混凝土．2006年第3期．88-90
16 孙柏峰．大体积混凝土浇筑后裂缝控制及降温保温工艺探讨．安徽建筑．2004年第2期．82-83
17 齐有章．大体积混凝土结构裂缝控制探讨．铁道建筑．2006年3期．97-98
18 秦春芳．建筑施工安全技术手册．中国建筑工业出版社．1991年
19 金信．建筑企业管理学．2．中国建筑工业出版社．2004年
20 成行、孔卓．大体积混凝土裂缝产生原因及控制措施．低温建筑技术．2005年第5期．112-113
21 叶琳昌、沈义．大体积混施工．中国建筑工业出版社．1986年
22 吴中伟、廉慧珍．高性能混凝土．中国铁道出版社．1999年
23 王刚、肖小玲．大体积混凝土裂缝的原因及控制．四川建筑．2004年第4期．102-103
24 白洪江．大体积混凝土裂缝控制措施．铁道建筑技术．2006年1期．65-67
25 陈金德．筏基大体积混凝土的裂缝控制．山西建筑．2006年9期．122-123
26 刘德慧．西宁某高层建筑基础大体积混凝土的温度裂缝控制技术．青海大学学报．第24卷第3期．12-14页
27 李苑．大体积混凝土温度裂缝控制．建筑技术．第37卷第4期．290-292
28 薛礼兵、王旭峰．大体积混凝土温度裂缝在实际工程中的控制技术．结构工程师．第22卷第4期．86-93
29 卞国祥、孙谨、于军．深圳会议展览中心大体积混凝土施工及长墙的裂缝控制．建筑技术．第35卷第4期．274-276
30 吴培明．混凝土结构上册(上册)．武汉工业大学出版社．2001年
31 李亚东．新编土木工程专业英语．西南交通大学出版社．2000年