一五零电厂50MW机组汽轮机转子裂纹分析及处理
摘要
由于电力体制改革和中国能源政策的现状,许多超期服役的机组仍然在线运行,这些机组的安全问题是不容忽视的。汽轮机转子安全性能及安全裕度直接影响到了整个机组的寿命,研究汽轮机转子裂纹是研究汽轮机寿命的一种重要手段。在本文中,通过研究引起汽轮机转子产生裂纹的原因及产生裂纹的过程,确定一个低周疲劳周次应力的振幅,计算出汽轮机转子的致裂周期和残余寿命;通过对汽轮机温度场和机械应力场的研究,得出各种工况下对机组寿命的损耗量,合理安排机组的启停方案;通过对已裂转子的裂纹处理方案的对比研究,确定经过车削后,强度最大而转子表面综合应力最小的方案,为转子裂纹处理提供明确的依据。
Because of the reform and the present status of China's energy policy, many units of extended active duty are still on their service-line. Safety of these units can not be ignored. The safety performance and safety margin of turbine directly influence the life of the whole unit. So the research of turbine rotor crack is an important mean for life. In this paper, through studying the causes and the process of turbine rotor crack, we can identify a low-cycle fatigue cycles stress amplitude and calculate turbine rotor fracturing cycle and the residual life; through studying turbine temperature and mechanical stress field,. we can get the loss of unit life under various conditions and reasonably arrangement unit start-stop program; through studying comparative treatment program of cracked rotor, we can get the program of the greatest strength and the smallest stress of the rotor surface after turning .Furthermore, we can get a clear basis for rotor cracks treatment.
Because of the reform and the present status of China's energy policy, many units of extended active duty are still on their service-line. Safety of these units can not be ignored. The safety performance and safety margin of turbine directly influence the life of the whole unit. So the research of turbine rotor crack is an important mean for life. In this paper, through studying the causes and the process of turbine rotor crack, we can identify a low-cycle fatigue cycles stress amplitude and calculate turbine rotor fracturing cycle and the residual life; through studying turbine temperature and mechanical stress field,. we can get the loss of unit life under various conditions and reasonably arrangement unit start-stop program; through studying comparative treatment program of cracked rotor, we can get the program of the greatest strength and the smallest stress of the rotor surface after turning .Furthermore, we can get a clear basis for rotor cracks treatment.
引文
[1]卢艳辉.曲轴裂纹的试验模态参数识别方法研究.[硕士学位论文].武汉:武汉理工大学,2004,2
[2]徐敏等.设备故障诊断手册.西安:西安交通大学出版社,1998. 189～198
[3]姚磊江. 疲劳损伤过程的能量耗散分析及基于能量耗散的疲劳损伤模型.西安:西北工业大学[博士论文],2000
[4]汽轮机故障诊断技术. 北京:李录平. 中国电力出版社, 2001,2～3
[5]魏先英,余耀 .125MW 汽轮机转子寿命损耗在线计算.发电设备, 1994,6:25～29
[6]吕涛,杨晓华,李年. 2Cr13 钢低周疲劳损伤演变规律研究. 机械强度,1999,21(2):118～121
[7]杜百平,李年,杨晓华. 服役损伤对汽轮机末级叶片断裂性能的影响. 机械强度,1997,19(04):42～45
[8]黄树红. 汽轮机转子低周疲劳寿命的可靠性设计.汽轮机技术,1991,(3).38～41
[9]程相利,马致远.汽轮机高压转子启停热应力场和寿命损耗计算.汽轮机技术 ,1992,(4):14～19
[10]安江英,周兰欣,张保衡. 两条转子钢疲劳曲线的比较分析研究. 汽轮机技术,1999,41(3):189～192
[11]安江英,张保衡.关于汽轮机转子寿命预测中的若干问题.华北电力大学学报(自然科学版),1996,(4):68～73
[12]安江英,周兰欣,张保衡. 两条转子钢疲劳曲线的比较分析研究. 汽轮机技术,1999,41(3):189～192
[13]金万里.超期服役机组的损伤模型研究及寿命评估分析.动力工程,2001,21(4):1292～1294
[14]Jian Ping Jing,Yi Suna,Song Bo Xia,et al. A continuum damage mechanics model on low cycle fatigue life assessment of steam turbine rotor. International Journal of Pressure Vessels and Piping,2001,78:59～64
[15]金尧,孙亚芳,孙训方. 蠕变疲劳共同作用下寿命估算方法. 材料工程,2000,11:6～8
[16]江宁,曹祖庆,肖建祥. 125 MW 汽轮机两班制启停若干问题分析. 华东电力,1999,7:24～27
[17]江宁,曹庆祖. 温态、热态启动中的最佳温度匹配方式探讨. 中国电机工程学报,1999,19(9):57～60
[18]陈坚红,阮伟,任浩仁. 冷态启动温升率对汽轮机转子寿命影响的研究. 动力工程, 1997,17(6):12～17
[19]周宇阳,陈汉平.汽轮机强制冷却过程参数控制及优化.中国电机工程学报,2000,20(1):72～76
[20]吴志锋,周宇阳,陈汉平. 600MW 汽轮机空气强制冷却时高中压转子热应力比较. 上海汽轮机,2000,4:8～12
[21]荆建平,武新华,夏松波.冷启动工况汽轮机转子的疲劳损伤.热能动力工程,2000,15(90):598～600
[22]支小牧,寇可新,曹向欣.汽轮机转子热应力在线监测、寿命管理及优化启动的研究.动力工程,2000,38(1):160～163
[23]钟礼金,郑碧芬.珠海发电厂 700MW 汽轮机强制冷却操作分析. 广东电力,2002,15(2):20～32
[24]任容.汽轮机在线寿命管理及优化启动的研究:[硕士学位论文].杭州:浙江大学.2002
[25]胥建群,庄贺庆.汽轮机转子材料 FATT 的试验研究 .东南大学学报(自然科学版),1991,21(2).114～117
[26]张晓欣,姜风春.动态断裂韧性测试系统的建立.哈尔滨工程大学学报,2000,21(6).30～33,38
[27]史进渊,袁伯英.汽轮机 17CrMo1V 材料焊接低压转子脆性断裂的研究.中国电机工程学报,2000,20(6).61～64
[28]孙茂才.金属力学性能.哈尔滨:哈尔滨工业大学出版社.2005,165～196
[29]王戟.金属材料及热处理.北京:中国劳动社会保障出版社.2004,132～152
[30]安江英,梁双印,张保衡. 材料软化对汽轮机转子使用寿命的影响. 中国电力,1997,30(1):52～54
[31]陈传尧,高大兴. 疲劳断裂基础.武汉:华中理工大学出版社,1991,7.201～215
[32]王坤 .大型汽轮机寿命问题研究:[博士学位论文].武汉:华中理工大学,2004
[33]王治国,郑承刚.DEH 数字电液在 50MW 汽轮机上的应用.河北电力技术,2004,4.35～36
[34]DL/T654-1998,火电厂超期服役机组寿命评估技术导则.[S].
[35]裴世英.从转子热应力角度合理安排汽轮机的超速试验.热力发电,1982,4:32～33
[36]王治国.汽轮机转子裂纹原因分析及运行安全措施.河北电力技术,2005,1:23～23,45
[37]传热学.北京.杨世铭,高等教育出版社, 1994,220～233
[38] 高 志 军 .600MW 汽 轮 机 转 子 冷 态 启 动 热 应 力 计 算 与 分 析 . 汽 轮 机 技术,2005,47(4):269～270
[39]黄山鹤,黄树红,王坤.分析强制冷却对 200MW 汽轮机高压转子寿命损耗的影响.广东电力,2005,(3):16～20,59
[40]裴世英.从转子热应力角度合理安排汽轮机的超速试验.热力发电,1982,(4):32～33
[41]鲍旭东.310MW 核电汽轮机启停中胀差趋势的分析.华东电力,2003,(7):52～54
[42]王建梅,蔡锴,卫国涛,等.调峰汽轮机转子热应力及寿命损耗在线检测系统.汽轮机技术,2001,43(5):298～300
[43]杨继明,陈冬林.300MW 机组变负荷调峰汽轮机转子寿命计算.湖南电力,2000,(2):7～10
[42]S. Suresh. 材料的疲劳. 国防工业出版社,1999,218～221
[43]R. Viswanathan. Damage Mechanisms and life assessment of High-Temperature Componets. ASM International,1989
[44]黄山鹤,黄树红,王坤.分析强制冷却对 200MW 汽轮机高压转子寿命损耗的影响.广东电力,2005,(3):16～20,59
[45] 杨 继 明 . 调 峰 机 组 汽 轮 机 转 子 剩 余 寿 命 的 合 理 分 配 方 案 . 汽 轮 机 技术,2004,(2):125～128
[45]杨继明,绪详,陈玉林.材料硬度值下降对汽轮机转子寿命消耗计算的影响. 热能动力工程,2003,18(4):372～374
[46]杨继明.材料硬度下降对汽轮机转子寿命消耗计算的影响.热能动力工程,2003,18(4):372～374
[47]杨继明,袁瑞,邓润亚.汽轮机转子低周疲劳寿命消耗计算及分析.东北电力技术,2003,(5):1～4
[48]王坤 .大型汽轮机寿命问题研究: [博士学位论文].武汉:华中理工大学.2004
[49]胥建群,周克毅,陈锦涛. 基于材料老化和蠕变疲劳交互作用汽轮机转子寿命预测.汽轮机技术 ,2003,(06):405～407,410
[50]胥建群,周克毅,陈锦涛. 基于材料老化和蠕变疲劳交互作用汽轮机转子寿命预测.汽轮机技术 ,2003,(6):405～407,410
[51]荆建平,孟光.汽轮机转子疲劳-蠕变损伤的非线性损伤力学分析.汽轮机技术,2003, (5).260～264
[52] 安 江 英 , 张 保 衡 . 材 料 脆 化 对 汽 轮 机 转 子 残 余 寿 命 的 影 响 . 电 力 情报,1997,(1):53～56
[53]魏先英,余耀.125MW 汽轮机转子寿命损耗在线计算.发电设备,1994.(6):25～29
[54]杨巨生,常鑫,夏同棠.汽轮机转子寿命的研究. 太原理工大学学报 ,2001,3 32(2):124～127
[55]魏先英,余耀.125MW 汽轮机转子寿命损耗在线计算.发电设备,1994.6:25～29
[56]翁思义.自动控制系统计算机仿真与辅助设计.西安:西安交通大学出版社.1987.1～95
[57] 杨 巨 生 , 常 鑫 , 夏 同 棠 . 汽 轮 机 转 子 寿 命 的 研 究 . 太 原 理 工 大 学 学报 ,2001,32(2):124～127
[58]王晓杰. 600MW 汽轮机冷态启动的寿命.汽轮机技术,1998,(5):269～271
[59] 杨 巨 生 , 常 鑫 , 夏 同 棠 . 汽 轮 机 转 子 寿 命 的 研 究 . 太 原 理 工 大 学 学报 ,2001,32(2):124～127
[60]夏同棠.汽轮机转子温度仿真研究. 中国电机工程学报,1996,16(1):5～9
[61]GB/T15248-94.金属材料轴向等幅低周疲劳试验方法,国家技术监督局,1995
[62]林晓斌,Roderick A.Smith.形状不规则裂纹的疲劳寿命预测技术. 中国机械工程, 1998,9(11):43～45
[63]王坤 .大型汽轮机寿命问题研究:[博士学位论文].武汉:华中理工大学.2004
[64]王坤,黄树红,陈小东,等.基于非线性累计准则的汽轮机转子可靠性定寿.华中科技大学学报(自然科学版),2002,30(5):59～61
[65]Songyuan Lu. A Method for calculating Damped Critical Speeds and Stability of Rotor-Bearing Systems. ASME Paper No.85-DET 116.Cincinnati,1985: 66~68
[66]Bathe ,K.J. and Wilson, e.l. Numerical Methods in Finite Element Analysis. John Wiley Publishers,1988: 25~29
[67]Lee C K. Theory of laminated piezoelectric plates for the design of distribute dsensors/actuators. Part I: governing equation sandreci procal relation ships. Journal of Acoustic Soc Am, 1990, 87(3): 1144~1158
[68]Yu Y Y. Some recent advances in linear and nonlinear dynamical modeling of elastic and piezoelectric plates. Adaptive Structures and Material System, 1993,35:185~195
[69]Chow C L, Wang J. A naniso tropic theory of elasticity for continuum damage mechanics. International Journal of Fracture, 1987, 33:3~16
[70]Chow C L, Wang J. An anisotropic theory of continuum damage mechanics for ductile fracture. Engineering Fracture Mechanics, 1987, 27(5): 547~558 [71)Valliappan S, Murit V, Zhang W H. Finite element analysis of anisotropic damage mechanics problems. Engineering Fracture Mechanics, 1990, 35(6):1061~107,151
[72]M. L. A . dams. Lecture Notes-Troubleshooting Power Plant & Rotating Machinery Vibration. Ohio: Machinery Vibration Institute, Cleveland.1990: 34~35
[2]徐敏等.设备故障诊断手册.西安:西安交通大学出版社,1998. 189～198
[3]姚磊江. 疲劳损伤过程的能量耗散分析及基于能量耗散的疲劳损伤模型.西安:西北工业大学[博士论文],2000
[4]汽轮机故障诊断技术. 北京:李录平. 中国电力出版社, 2001,2～3
[5]魏先英,余耀 .125MW 汽轮机转子寿命损耗在线计算.发电设备, 1994,6:25～29
[6]吕涛,杨晓华,李年. 2Cr13 钢低周疲劳损伤演变规律研究. 机械强度,1999,21(2):118～121
[7]杜百平,李年,杨晓华. 服役损伤对汽轮机末级叶片断裂性能的影响. 机械强度,1997,19(04):42～45
[8]黄树红. 汽轮机转子低周疲劳寿命的可靠性设计.汽轮机技术,1991,(3).38～41
[9]程相利,马致远.汽轮机高压转子启停热应力场和寿命损耗计算.汽轮机技术 ,1992,(4):14～19
[10]安江英,周兰欣,张保衡. 两条转子钢疲劳曲线的比较分析研究. 汽轮机技术,1999,41(3):189～192
[11]安江英,张保衡.关于汽轮机转子寿命预测中的若干问题.华北电力大学学报(自然科学版),1996,(4):68～73
[12]安江英,周兰欣,张保衡. 两条转子钢疲劳曲线的比较分析研究. 汽轮机技术,1999,41(3):189～192
[13]金万里.超期服役机组的损伤模型研究及寿命评估分析.动力工程,2001,21(4):1292～1294
[14]Jian Ping Jing,Yi Suna,Song Bo Xia,et al. A continuum damage mechanics model on low cycle fatigue life assessment of steam turbine rotor. International Journal of Pressure Vessels and Piping,2001,78:59～64
[15]金尧,孙亚芳,孙训方. 蠕变疲劳共同作用下寿命估算方法. 材料工程,2000,11:6～8
[16]江宁,曹祖庆,肖建祥. 125 MW 汽轮机两班制启停若干问题分析. 华东电力,1999,7:24～27
[17]江宁,曹庆祖. 温态、热态启动中的最佳温度匹配方式探讨. 中国电机工程学报,1999,19(9):57～60
[18]陈坚红,阮伟,任浩仁. 冷态启动温升率对汽轮机转子寿命影响的研究. 动力工程, 1997,17(6):12～17
[19]周宇阳,陈汉平.汽轮机强制冷却过程参数控制及优化.中国电机工程学报,2000,20(1):72～76
[20]吴志锋,周宇阳,陈汉平. 600MW 汽轮机空气强制冷却时高中压转子热应力比较. 上海汽轮机,2000,4:8～12
[21]荆建平,武新华,夏松波.冷启动工况汽轮机转子的疲劳损伤.热能动力工程,2000,15(90):598～600
[22]支小牧,寇可新,曹向欣.汽轮机转子热应力在线监测、寿命管理及优化启动的研究.动力工程,2000,38(1):160～163
[23]钟礼金,郑碧芬.珠海发电厂 700MW 汽轮机强制冷却操作分析. 广东电力,2002,15(2):20～32
[24]任容.汽轮机在线寿命管理及优化启动的研究:[硕士学位论文].杭州:浙江大学.2002
[25]胥建群,庄贺庆.汽轮机转子材料 FATT 的试验研究 .东南大学学报(自然科学版),1991,21(2).114～117
[26]张晓欣,姜风春.动态断裂韧性测试系统的建立.哈尔滨工程大学学报,2000,21(6).30～33,38
[27]史进渊,袁伯英.汽轮机 17CrMo1V 材料焊接低压转子脆性断裂的研究.中国电机工程学报,2000,20(6).61～64
[28]孙茂才.金属力学性能.哈尔滨:哈尔滨工业大学出版社.2005,165～196
[29]王戟.金属材料及热处理.北京:中国劳动社会保障出版社.2004,132～152
[30]安江英,梁双印,张保衡. 材料软化对汽轮机转子使用寿命的影响. 中国电力,1997,30(1):52～54
[31]陈传尧,高大兴. 疲劳断裂基础.武汉:华中理工大学出版社,1991,7.201～215
[32]王坤 .大型汽轮机寿命问题研究:[博士学位论文].武汉:华中理工大学,2004
[33]王治国,郑承刚.DEH 数字电液在 50MW 汽轮机上的应用.河北电力技术,2004,4.35～36
[34]DL/T654-1998,火电厂超期服役机组寿命评估技术导则.[S].
[35]裴世英.从转子热应力角度合理安排汽轮机的超速试验.热力发电,1982,4:32～33
[36]王治国.汽轮机转子裂纹原因分析及运行安全措施.河北电力技术,2005,1:23～23,45
[37]传热学.北京.杨世铭,高等教育出版社, 1994,220～233
[38] 高 志 军 .600MW 汽 轮 机 转 子 冷 态 启 动 热 应 力 计 算 与 分 析 . 汽 轮 机 技术,2005,47(4):269～270
[39]黄山鹤,黄树红,王坤.分析强制冷却对 200MW 汽轮机高压转子寿命损耗的影响.广东电力,2005,(3):16～20,59
[40]裴世英.从转子热应力角度合理安排汽轮机的超速试验.热力发电,1982,(4):32～33
[41]鲍旭东.310MW 核电汽轮机启停中胀差趋势的分析.华东电力,2003,(7):52～54
[42]王建梅,蔡锴,卫国涛,等.调峰汽轮机转子热应力及寿命损耗在线检测系统.汽轮机技术,2001,43(5):298～300
[43]杨继明,陈冬林.300MW 机组变负荷调峰汽轮机转子寿命计算.湖南电力,2000,(2):7～10
[42]S. Suresh. 材料的疲劳. 国防工业出版社,1999,218～221
[43]R. Viswanathan. Damage Mechanisms and life assessment of High-Temperature Componets. ASM International,1989
[44]黄山鹤,黄树红,王坤.分析强制冷却对 200MW 汽轮机高压转子寿命损耗的影响.广东电力,2005,(3):16～20,59
[45] 杨 继 明 . 调 峰 机 组 汽 轮 机 转 子 剩 余 寿 命 的 合 理 分 配 方 案 . 汽 轮 机 技术,2004,(2):125～128
[45]杨继明,绪详,陈玉林.材料硬度值下降对汽轮机转子寿命消耗计算的影响. 热能动力工程,2003,18(4):372～374
[46]杨继明.材料硬度下降对汽轮机转子寿命消耗计算的影响.热能动力工程,2003,18(4):372～374
[47]杨继明,袁瑞,邓润亚.汽轮机转子低周疲劳寿命消耗计算及分析.东北电力技术,2003,(5):1～4
[48]王坤 .大型汽轮机寿命问题研究: [博士学位论文].武汉:华中理工大学.2004
[49]胥建群,周克毅,陈锦涛. 基于材料老化和蠕变疲劳交互作用汽轮机转子寿命预测.汽轮机技术 ,2003,(06):405～407,410
[50]胥建群,周克毅,陈锦涛. 基于材料老化和蠕变疲劳交互作用汽轮机转子寿命预测.汽轮机技术 ,2003,(6):405～407,410
[51]荆建平,孟光.汽轮机转子疲劳-蠕变损伤的非线性损伤力学分析.汽轮机技术,2003, (5).260～264
[52] 安 江 英 , 张 保 衡 . 材 料 脆 化 对 汽 轮 机 转 子 残 余 寿 命 的 影 响 . 电 力 情报,1997,(1):53～56
[53]魏先英,余耀.125MW 汽轮机转子寿命损耗在线计算.发电设备,1994.(6):25～29
[54]杨巨生,常鑫,夏同棠.汽轮机转子寿命的研究. 太原理工大学学报 ,2001,3 32(2):124～127
[55]魏先英,余耀.125MW 汽轮机转子寿命损耗在线计算.发电设备,1994.6:25～29
[56]翁思义.自动控制系统计算机仿真与辅助设计.西安:西安交通大学出版社.1987.1～95
[57] 杨 巨 生 , 常 鑫 , 夏 同 棠 . 汽 轮 机 转 子 寿 命 的 研 究 . 太 原 理 工 大 学 学报 ,2001,32(2):124～127
[58]王晓杰. 600MW 汽轮机冷态启动的寿命.汽轮机技术,1998,(5):269～271
[59] 杨 巨 生 , 常 鑫 , 夏 同 棠 . 汽 轮 机 转 子 寿 命 的 研 究 . 太 原 理 工 大 学 学报 ,2001,32(2):124～127
[60]夏同棠.汽轮机转子温度仿真研究. 中国电机工程学报,1996,16(1):5～9
[61]GB/T15248-94.金属材料轴向等幅低周疲劳试验方法,国家技术监督局,1995
[62]林晓斌,Roderick A.Smith.形状不规则裂纹的疲劳寿命预测技术. 中国机械工程, 1998,9(11):43～45
[63]王坤 .大型汽轮机寿命问题研究:[博士学位论文].武汉:华中理工大学.2004
[64]王坤,黄树红,陈小东,等.基于非线性累计准则的汽轮机转子可靠性定寿.华中科技大学学报(自然科学版),2002,30(5):59～61
[65]Songyuan Lu. A Method for calculating Damped Critical Speeds and Stability of Rotor-Bearing Systems. ASME Paper No.85-DET 116.Cincinnati,1985: 66~68
[66]Bathe ,K.J. and Wilson, e.l. Numerical Methods in Finite Element Analysis. John Wiley Publishers,1988: 25~29
[67]Lee C K. Theory of laminated piezoelectric plates for the design of distribute dsensors/actuators. Part I: governing equation sandreci procal relation ships. Journal of Acoustic Soc Am, 1990, 87(3): 1144~1158
[68]Yu Y Y. Some recent advances in linear and nonlinear dynamical modeling of elastic and piezoelectric plates. Adaptive Structures and Material System, 1993,35:185~195
[69]Chow C L, Wang J. A naniso tropic theory of elasticity for continuum damage mechanics. International Journal of Fracture, 1987, 33:3~16
[70]Chow C L, Wang J. An anisotropic theory of continuum damage mechanics for ductile fracture. Engineering Fracture Mechanics, 1987, 27(5): 547~558 [71)Valliappan S, Murit V, Zhang W H. Finite element analysis of anisotropic damage mechanics problems. Engineering Fracture Mechanics, 1990, 35(6):1061~107,151
[72]M. L. A . dams. Lecture Notes-Troubleshooting Power Plant & Rotating Machinery Vibration. Ohio: Machinery Vibration Institute, Cleveland.1990: 34~35