摘要
【目的】研究溶胶-凝胶法制备纳米ZnO的相关条件,纳米ZnO熔附于HAPw的工艺参数,制备出具有粗糙表面的HAPw/ZnO填料,进一步研究HAPw/ZnO复合填料对口腔常见致病菌的抗菌性能,以期为下一步制备抗菌性填料奠定基础。
【材料和方法】采用溶胶-凝胶法制备纳米ZnO,研究不同PH值、不同表面改性剂用量及不同环已烷用量对生成纳米ZnO粒径大小、分散情况及抗菌性能的影响:在确定纳米ZnO制备工艺条件下,将纳米ZnO通过一定工艺熔附于陶瓷晶须表面,通过TEM观察HAPw/ZnO填料复合体的形貌;用液体稀释法检测四种无机填料(自制纳米ZnO、HAPw/ZnO,商品纳米ZnO,四针状氧化锌晶须)对口腔常见致病菌的抗菌性能。
【结果】在PH值为8.2,油酸量与总醇溶液量比例为0.0015,环已烷量为总醇溶液1/2时制备的纳米ZnO纳米粒径小,分散性好;以此条件下制备的纳米ZnO胶体通过一定工艺可熔附于HAPw上,实现晶须的改性;抗菌性能显示自制的纳米ZnO、HAPw/ZnO,商品纳米ZnO,四针状氧化锌晶须四种抗菌剂均具备一定的抗菌性其中自制纳米ZnO抗菌性能最好。
【结论】醋酸锌醇溶液在溶胶-凝胶条件下可以制备出纳米ZnO;通过溶胶-凝胶法制备的纳米ZnO可以用来改性HAPw;HAPw经纳米ZnO改性后具备一定的抗菌性。
[Objectives] The aim of the study was to investigate the process condition of sol-gel process of ZnO-related condition.The preparation parametes of nano Zinc Oxide was fused on the HAPw. Prepared with a rough surface HAPw/ZnO filler. Further research HAPw/ZnO composite fillers on the antibacterial properties of oral pathogens in order to prepare for the next lay the foundation for antibacterial filler.
[Materials and Methods] Sol-gel process and ZnO, of different PH values, different dosage and different surface modification on the formation of nano ZnO cyclohexane particle size, dispersion and antibacterial properties; Preparation of nano-ZnO in determining the conditions, the nano-ZnO by a certain process-fused ceramic whiskers on the surface.Through TEM observation HAPw/ ZnO complex morphology of filler. Dilution test with four kinds of inorganic fillers (ZnO, HAPw/ ZnO, zinc oxide products, four needle-like zinc oxide whiskers) of oral cariogenic bacteria commonly have antibacterial properties.
[Result] In the PH value of 8.2, Oleic acid content and the proportion of the total volume of alcoholic solution is 0.0015, the total amount of alcohol solution of cyclohexane 1/2 diameter of the nano ZnO, Nano-particle size is small, good dispersion.Under this condition ZnO colloid prepared as liquor, will be cleaned HAPw into the ZnO colloidal solution containing,40℃and 60% relative humidity for three days, Drying, calcinations, under the insulation in the whisker surface layer of ZnO colloidal crystals grown film. Antibacterial properties of zinc oxide that the Self,HAPw/ZnO, commodity zinc oxide, zinc oxide whiskers tetrapod all four antimicrobial agents have certain antibacterial properties.
[Conclusions] Alcohol solution of zinc acetate in the sol-gel can be prepared under the conditions of small particle size zinc oxide nanoparticles. ZnO whiskers formed on the surface in a layer of ceramic membrane generated HAPw/ZnO has certain antibacterial properties.
引文
1.蔡晓慧,朱广山,高波,等.Ag/SBA-15复合材料的制备及其抗菌性质[J].高等学校化学学报,2006,27(11):2042-2044.
2. L Spanhel, MA Anderson. Semiconductor Cluster in the Sol-Gel Process Quantized Aggregation, Gelation and Crystal Growth in Concentrated ZnO fColloid[J].J Am Chem Sic,1991,113(8):2826-2833.
3. Eric A.Meulenkamp, Synthesis and Growth of ZnO nanoparticle [J].J Phys Chem B,1998,102(29):5566-5572
4. V Noack,A Eychmuller. Annealing of Nanometer-sized Zinc Oxide Particles [J]. Chem Mater,2002,14(3):1411-1417.
5. Dong Qian, JZ Jiang, et al. Preparation of ZnO nanocrystals via ultrasonic irradiation [J].Chem Commun,2003,7(9):1078-1079.
6. J Sawai, H Igarashi, A Hashimoto, et al. Evaluation of growth inhibitory effect of ceramics powder slurry on bacteria by conductance method [J]. JCEJ,1995,28(5):556-561.
7. J Sawai, Quantitative evaluation of antibacterial activities of metallic oxide powders(ZnO, MgO and CaO)by conductimetric assay[J]. J Microbiol Methods,2003,54 (3):177-182.
8. Yamamoto O. Influence of particle size on the antibacterial activity of zinc oxide[J].Int J Inorg mater.2001,7(3):643-646
9. N. Bouropoulos, I. Tsiaoussis, P. Poulopoulos, et al. ZnO controllable sized quantum dots produced by polyol method:An experimental and theoretical study. Materials Letters,2008,62(8)3533-3535.
10.沈琳,赵宗斌,邓文雅.溶胶-凝胶法合成Zn0纳米材料及其抗菌性能研究[J].功能材料.2007,11(38):1908-1911.
11.王世敏,许祖勋,傅晶.纳米碳管/聚合物复合材料的研究进展[J].胶体和聚合物,2002,20(2):135-137.
12.韩丽华,金建新,等.纳米SnO2粉体团聚的控制[J].材料开发与应用,2005,20(6):30-33.
13.李春喜,王子镐.超声技术在纳米材料制备中的应用[J].化学通报,2001,64(5):268-271.
14. J Sawai, H Kojima, H Igarashi, et al. Bactericidal action of calcium oxide powder[J]. Trans Mater Res soc Jpn,1999,24(6):667-670.
15. J Sawai, H.Igarashi, A.Hashimoto,et al.Effect of particle size and heating temperature of ceramic powders on antibacterial activity of their slurries. Journal Of Chemical Engineering of Japan,1996,29(2):251-256.
16. C Karunakaran, S Senthilvelan, S Karuthap. Solar photooxidation of aniline on ZnO surfaces[J].Solar Energy Materials&Solar Cells,2005.89(5):391-402.
17. M Descamps, JC Hornez,A Leriche. Manufacture of hydroxyapatite beads for medical applications[J].J Eur Ceram Soc,2009,29(3):369-375.
18. N Bouropoulos, I Tsiaoussis, P Poulopoulos. et al. ZnO controllable sized quantum dots produced by polyol method:An experimental and theoretical study[J].Mater Letters,2008,62(8):3533-3535.
1.杨晓庆,李玉宝.医用羟基磷灰石/二氧化钛纳米复合材料的制备及性能研究[J].中国现代医学杂志,2003,13(5):26-28.
2. Li Yubao, J deWijn, C.EA.T. Klein, et al.Preparation and characterization of nanograde osteoapatite-like Rod Crystals. J Mater Sci:Materials in Medicine,1994,5(5):252-255
3.李玉宝,魏杰.纳米生物医用材料及其应用.中国医学科学院学报,200224(2):209-212
4. A Rapaez-Kmita,A S16sarczyk,Z Paszkiewicz.et al.HAP-ZrO2 composite coatings prepared by plasma spraying for biomedical applications[J].Ceram Inter.2005,31(4):567-571
5. Taya M,Hayshi AS,Kobayashi AS.Toughening of a Particulate-Reinforced Ceramic-Matrix Composite by Thermal Residual Stress [J].J Am Ceram Soc,1990,73(5):1382-1391.
6. A Rapaez-Kmita,A Slosarczyk,Z Paszkiewicz.et al.Evaluation of HAP-ZrO2 composites and monophase HAP bioceramics.In vitro study[J].J Mol Struct,2004,39(18):5865-5867.
7. Wang ZQ, Xue DF, Chen XX, et al. Mechanical and biomedical properties of hydroxyapatite-based gradient coating on α-Al2O3 ceramic substrate [J].J Non-Cryst solids,2005,351 (19-20):1675-1681.
8. Bray DJ. Annual minerals review silicon carbide whiskers. Am Cerm Soc Bull,1993,72(6):116
9.潘金生,陈永华.晶须及其应用.复合材料学报,1995,24(7):1-7
10.师吕绪主编,材料大词典.北京:化学工业出版社,1994.480-482
11.高伟,陈寰贝,陈庆华等.表面改性羟基磷灰石晶须填料增强牙科复合树脂[J].广西轻工业2009,124(3):28-30.
12.张文云,李星星,陈庆华等.正砖酸乙酯改性牙科复合树脂填料的表征及其弯曲强度[J].中国组织工程研究与临床康复,2008,12(49):968-969.
13.张文云,李星星,袁艳波等.晶须熔附条件对晶须增强复合树脂性能的影响[J].口腔医学研究,2009,25(4):397-399.
14.叶青,胡仁,林种玉,等.羟基磷灰石与牛血清白蛋白相互作用的原位红外光谱研究[J].高等学校化学学报.2006,27(8):1552-1554.
15. M Okazaki, M Sato, J Takahashi.Space-cutting model of Hydroxyapatite [J].Bioaterials,1995,16(1):45-49.
16. M Descamps, J.C.Hornez, A.Leriche. Manufacture of hydroxypatite beads for medical applications[J].J Eur Ceram Soc,2009,29(3):369-375.
17. Zhengpeng Yang, Chunjing Zhang. Absorption/desorption behavior of protein on nanosized hydroxyapatite coatings:A quartz crystal microbalance study [J].Appl Surf Sci,2009,255(8):4569-4574.
18.侯文生,戴晋明,魏丽升等.载银锌纳米SiO2抗菌剂[J].合成纤维工业,2004,27(13):111-114
1. Fang M, Chen JH, Xu XL,et al.Antibacterial activities of inorganic agents on six bacteria associated with oral infections by two susceptibility tests [J]. Int J Antimicrob Agents,2006,27(6):513-517
2. National Committee for Clinical Laboratary Standards. Approved Standard,6th ed.Document M11-A6, Methods for antimicrobial susceptibility testing for anaerobic bacteria. USA:NCCLS,2004
3. Kawai K, Tsuchitani Y. Effects of resin composite components on glucosyl transferase of cariogenic bacterium[J].J Biomed Mater Res.2000,51(1):123-127
4. Imazato S,Torii M,Tsuchitani Y.et al.Incorporation of bacterial inhibitor into resin composite[J].J Dent Res,1994,73:1437-1443
5. 佘文君,张富强.6种纳米级载银无机抗菌剂对口腔病原菌的抗菌活性比较[J].上海口腔医学,2003,12(5):356-358
6. 李蓓,赵铱民,杨聚才,等.比较纳米载银抗菌剂与纳米二氧化钛抗菌剂抗白色念珠菌性能的实验研究[J].临床口腔医学,2008,24(2):70-72.
7. 佘文君,张富强.6种纳米级载银无机抗菌剂对口腔病原菌的抗菌活性比较[J].上海口腔医学,2003,12(5):356-35
8. Yamamoto O. Influence of particle size on the antibacterial activity of zinc oxide[J].Int J Inorg mater.2001,7(3):643-646
9. 江华洲,李伟.羟磷灰石抗菌性涂层材料的研究[J].国际口腔医学杂志,2008,35(2):189-191.
10. Trapalis CC,Kokkoris M,Perdikakis G,et al. Study of Antibacterial Composite Cu/SiO2 Thin Coatings [J].J Sol-Gel Sci Tech,2003,26 (3): 1213-1218.
11.李炜罡,吕维平,王海滨,等.抗菌材料进展[J].化工新型材料,2003,31(3):7-10.
12.方明,陈吉华.不同种类无机抗菌剂对口腔致病菌抗菌性能比较及其检测方法探讨[J].口腔医学研究,2006,22(1):12-14
13.林英光,杨卓如,程江.纳米掺锶羟基磷灰石的制备及其抗菌性能研究[J].化工新型材料,2006,34(9):52-55.
14. Jeyachandran YL, Narayandass SK, Mangalaraj D,et al. A study on bacterial attachment on titanium and hydroxyapatite based films [J]. Surf Coat Technol,2006,201(6):3462-3474
1. Mjor LA, Moorhead JE, Dahl JE.Reasons for replacement of restorations in permanent teeth in general dental practice.Int Dent J,2000,50:361-366.
2. Condon JR, Ferracane JL.Reduced polymerization stress through non-bonded nanofillparticles[J]. Biomaterials,2002,23(18):3807-3815.
3. Xu HHK.Eiehmiller FC.Antonucci JM.et al.Dental resin composites containing ceramic whiskers and procured glass ionomer particle[J].Dental materials,2000,16 (5):356-363.
4. Xu HHK, Quirm JB, Smith DT, et al. Dental resin composites containing silica-fused whiskers-effects of whisker-to-silica ratio on fracture toughness and indentation properties[J].Biomaterials,2002,23(3):735-742
5. Walsh WR,Kim HD, JOng YS, et al.Controlled release of platelet-derived growth factor using ethylene vinyl acetate copolymer(EVAc) coated on stainless-steel wires[J].Biomaterials,1995.16(17):1319-1325.
6. Leinfelder KF.Do restorations made of amalgam outlast those made of resin-based composite?[J].Am J Dent.2000,13(4):192-194.
7. Hofmann N.Hunecke A. Influence of curing methods and matrix type on the marginal seal of class Ⅱ resin-based composite restorations in vitro[J].Oper Dent.2006,31 (1):97-105.
8. Chuang SF, Jin YT, Liu JK, et al. Influence of flowable composite lining thickness on Class II composite restorations[J].Oper Dent.2004,29(3):301-308.
9. Miguez PA.Pereira PN.Foxton RM. et al. Effects of flowable resin on bond strength and gap formation in Class I restorations [J].Dent Mater,2004.20(9):839-845.
10. Feilzer AJ, De Gee AJ, Davidson CL.Shrinkage stress in relation to cavity configuration [J].J Dent Res.1987.66(11):1636-1639.
11. Loguercio AD, Reis A.Ballester RY. Polymerization shrinkage:effects of constraint and filling technique in composite restorations[J].Dent Mater,2004,20(3):236-243.
12. Kuijs RH, Fennis WM, Kreulen CM, et al.Does layering minimize shrinkage stresses in composite restorations? [J].J Dent Res.2003,82(12):967-971.
13.Zmazato S,Kuramoto A.Takahashi Y.et a1.In.,itro antibacterial effects of the dentin primer of clearfil protect Bond[J].Dent Matcr.20()6.22:527-532
14. Stutsky H,Weiss El,Feuerstein O.Antibacterial p roperties of self-etching dental adhesive systems[J].J Am Dent Assoc.2007.138(3):349-354.
15.方明.陈吉华,徐修礼.等.不同种类无机抗菌剂对口腔致病菌抗菌性能比较及其测方法探讨[J].口腔医学研究,2006.22(1):12-14.
1. Takemura KSY. Staninec M. Antibacterial activity of a Bis-GMA based composite resin and antibacterial effect of chlorhexidine incorporation. [J].Jpn J Conserv Dent.1983.26:540-7.
2. 李玉芳,李明.塑料抗菌剂的研究开发进展[J].聚合物与助剂,2009,27(1):1-5.
3. Prudencio WRO, Rosa Helena MG, Rafael YB, et al. Zinc surface addition to glass-ionomer-based cements:influence on physical and antibacterial properties, zinc and fluoride release [J].Dent Mater.2003,19(3):212-217
4. Kawashita M,Tsuneyama S,Miyaji F, et al. Antibacterial silver-containing silica glass prepared by sol-gel method [J].Biomaterial,2000.21 (4):393-398.
5. Kawahara K,Tsuruda K,Morishita M.et al. Antibacterial effect of silver-zeolite on oral bacteria under anaerobic conditions[J].Dent Mater,2000.16(6):452-455.
6. Leung D, Spratt DA, Pratten J, et al.Chlorhexidine-releasing methacrylate dental composite materials[J].Biomaterials,2005,34 (26):7145-7153.
7. Imazato S, Ebi N, Takahashi Y, et al.Antibacterial activity of bactericide immobilized filler for resin-based restoratives[J].Biomaterial,2003.24(20):3605-3609.
8. 李凤艳,汪燮卿,陈拥军.等.交联结构对水不溶性聚季铵盐类杀菌性能的影响[J].应用化学,2000,17(5):566-569.
9. Noboru Ebi.Satoshi Imazato,Yuichiro Noiri.et al. Inhibitory effects of resin composite containing bactericide-immobilized filler on plaque accumulation[J]. Dental Mater,2001,17:485-491.
10. ParisienA,Allain B. Novel alternatives to antibiotics:bacte-riophages, bacterial cell wall hydrolases, and antimicrobial peptides [J].J Applied Microbioal. 2008,104(1):1-13.
11 蔡晓慧.朱广山,高波,等Ag/SBA-15复合材料的制备及其抗菌性质[J].高等学校化学学报.2006.27(11):2042-2044.
12. H Akiyama, OYamasaki, H Kanzaki, et al. Effects of zinc oxide on the attachment of Staphylococcus aureus strains[J].J dermatol sci.1998,17(1):67-74
13. KH Tam, AB Djurisic. CMN Chan, et al. Antibacterial activity of ZnO nanorods prepared by a hydrothermal method[J].Thin Solid Films.2007,516(8):6167-6174.
14.支华军,贺英.纳米ZnO的光催化和光致发光性能[J].材料导报,2004,18(1):47·49.
15. R Brayner. R Ferrari-lliou. Toxicological impact studies based on Escherichia colibacteria in ultrafine ZnO nanoparticles colloidal medium[J].Nano Letters.2006, 6(4):866-870.
16. N Bouropoulos, I Tsiaoussis. P Poulopoulos, et al. ZnO controllable sized quantum dots produced by polyol method:An experimental and theoretical study [J]. Materials Letters,2008.62 (8):3533-3535.
17. E Manias, A Touny, L wu, et al. Polypropylene/montmorillonite nano composites Review of the synthetic routes and materials properties[J].Chem Mater,2001, 13(10):3516-3523.
18.薛涛.曾舒.毛键等.铈掺杂纳米 ZnO抗菌粉的研制及其结构性能分析[J].中国稀十学报,2006.24(z1):45-48.