再生胶粉海绵的制备及其吸声特性的研究
|
摘要
本论文受国家自然科学基金-中国工程物理研究院联合基金项目资助,是导师所主持的自然科学基金委员会-中国工程物理研究院联合基金的资助项目(批准号10276031)研究的延伸。
本文研究了利用再生胶粉制备吸声材料,即制备再生胶粉海绵的方法。这项研究如果能够实现工业化,则既可以解决废弃橡胶的“黑色污染”问题,又可以减少噪声污染。
文章研究了不同的发泡剂用量、软化剂用量以及填料量对该材料吸声性能的影响。
研究分析表明,再生胶粉海绵在中高频段会出现吸收峰。当采用最佳配方时,再生胶粉海绵试样(厚度为10mm)的吸声系数在1115～3020Hz带宽内大于0.2,在1357-2409Hz带宽内大于0.4,特别是在1794～1893Hz带宽内,其吸声系数高达0.998。
The thesis is the further research of the project supported by NASF presided by adviser (No.10276031).
The thesis introduced the idea of making reclaimed crump rubber sponge which is used as sound absorption material. If this research could be industrialized, and it will not only solve the black pollution brought by scrap rubber but also decrease noise pollution.
The factors that different dosage of blowing agent, supple ointment and filling quantity influencing on the performance of acoustic characteristic of reclaimed crump rubber sponge are analysed in this thesis.
The research shows that the reclaimed crumb rubber possesses its sound absorption peak within intermediate and high frequency bandwidth. With the best proportion, sound absorption coefficients of this material are all above 0.2 from 1115Hz to 3020Hz and they are all above 0.4 from 1357Hz to 2409Hz and especially within bandwidth which is from 1794Hz to 1893Hz, the sound absorption coefficients are as high as 0.998.
本文研究了利用再生胶粉制备吸声材料,即制备再生胶粉海绵的方法。这项研究如果能够实现工业化,则既可以解决废弃橡胶的“黑色污染”问题,又可以减少噪声污染。
文章研究了不同的发泡剂用量、软化剂用量以及填料量对该材料吸声性能的影响。
研究分析表明,再生胶粉海绵在中高频段会出现吸收峰。当采用最佳配方时,再生胶粉海绵试样(厚度为10mm)的吸声系数在1115～3020Hz带宽内大于0.2,在1357-2409Hz带宽内大于0.4,特别是在1794～1893Hz带宽内,其吸声系数高达0.998。
The thesis is the further research of the project supported by NASF presided by adviser (No.10276031).
The thesis introduced the idea of making reclaimed crump rubber sponge which is used as sound absorption material. If this research could be industrialized, and it will not only solve the black pollution brought by scrap rubber but also decrease noise pollution.
The factors that different dosage of blowing agent, supple ointment and filling quantity influencing on the performance of acoustic characteristic of reclaimed crump rubber sponge are analysed in this thesis.
The research shows that the reclaimed crumb rubber possesses its sound absorption peak within intermediate and high frequency bandwidth. With the best proportion, sound absorption coefficients of this material are all above 0.2 from 1115Hz to 3020Hz and they are all above 0.4 from 1357Hz to 2409Hz and especially within bandwidth which is from 1794Hz to 1893Hz, the sound absorption coefficients are as high as 0.998.
引文
[1]黄秀莲.环境分析与检测.第1版.北京：高等教育出版社,1989,2.270。
[2]李海涛,朱锡,石勇等.多孔吸声材料的研究进展.材料科学与工程学报.2004,22(6).934。
[3]吕玉恒.国内噪声控制近况评述.噪声与振动控制.2001,(6).14-17。
[4]马大猷主编.噪声控制学.北京：科学出版社,1987.232-302。
[5]胡俊明.吸声材料在改善建筑声环境质量中的作用和发展趋势.噪声与振动控制.1993,(3).2-4。
[6]张守梅,曾令可,黄其秀等.环保吸声材料的发展动态及展望.陶瓷学报.2002,23(1).56～61。
[7]Croker Malcolm J. Noise and Noise Control CRC Press Ine.1982, (2). 21-22。
[8]胡俊民.发展吸声材料,提高环境质量.保温材料与节能技术.2002,(5).7-11。
[9]陈月辉.声学功能橡胶.特种橡胶制品.2004,(1).57-58。
[10]程桂萍,陈宏灯,何德坪等.多孔铝的声学性能.东南大学学报.1998,28(6)169-172。
[11]HJ Lee, S H Eom, Y K Song, S S Cho. [J]. Materials Science and Technology. 2003,19(6).819-825.
[12]余欢,方立高,严青松.[J]. HotWorking Technology,2001, (1).36-39。
[12]汤慧萍,张正德.金属多孔材料的发展现状.稀有金属材料与工程.1997,26(1).1-6。
[13]金卓仁.泡沫金属吸声材料的研究.噪声与振动控制.1993,6(3).31-35。
[14]Andrews E W, Gibson L J. The influence of cracks, notches and holes on the tensile strength of cellular solids. Acta Materialia.2001,5,49. 2975-2979。
[15]Mccormack T M, Miller R, Kelser G, et al. Failure of sandwich beams with metallic foamcores. Int J Solids and Structures.2001,38.4901～4920。
[16]程桂萍,陈宏灯,何德坪,等.多孔铝在不同介质中的吸声性能.噪声与振动控制.1998,(5).29-34。
[17]赵增典,张勇,苗汇静.泡沫铝的吸声性能初探.兵器材料科学与工程.1998, 28(1).48-52。
[18]王月.孔结构对通孔泡沫铝水声吸声性能的影响.材料开发与应用.2001,(4)1624-1627。
[19]钱军民,李旭祥.聚合物岩棉发泡复合材料吸声性能的研究.材料开发与应用.2006,6,15(3).15-18。
[20]曾晓东,李旭祥,席莺等.聚氯乙烯-岩棉复合发泡吸声材料的研制.化工新型材料.1998,(5).37～42。
[21]洪宗辉主编.环境噪声控制工程.北京：高等教育出版社,2002.118-144。
[22]马保国,朱洪波,董荣珍.高效吸声材料的研制.新型建筑材料.2002,(5).42-43。
[23]周曦亚,凡波.吸声材料研究的进展.中国陶瓷.2004,10,40(5).26～27。
[24]刘伯伦,钟祥璋.提高多孔材料低频吸声性能的探讨.声学技术.1992,11.57-60。
[25]H. C. Strifors and GC. Gaunaurd. Wave propagation in isotropic lineary isoelastic media. J.Acoust.Soc.Am.1959,85.995～1004。
[26]P. C. Waterman and R.Truell. Multiple scattering of waves. J. Mach.Phy.1961,vol2. 512-537.
[27]G C. Gaunaurd and H. Uberall. Resonance theory of the effective properties of perforated solids. J. Acoust. Soc. Am.1982, vol71(2).282～295。
[28]G C. Gaunaurd and J. Barlow. Matrix viscosity and cavity-size distribution effective properties of perforated elastomers. J.Acoust.Soc.Am.1984, vol 75(1).23～34。
[29]R. L. Kliginan.,W. M. Madigosky and J. R. Barlow. Effective dynamic properties of composite viscoelastic materials. J. Acoust. Soc. Am.1982, vol 70(5).1437～ 1444。
[30]G C. Gaunaurd and W. Waterman. Comparison of effective medium theories for inhomogeous continua. J. Acoust. Soc. Am.1989,vol85(2).541～554。
[31]F.H.Kerr. The scattering of a plane elastic wave by spherical elasticinclusions. Int. J. Engng Sci.1992, vol30(2).169～186。
[32]赵光贤,任文坛.中国橡胶.2005,21(20).23-24。
[33]张殿荣,马占兴,杨清芝.现代橡胶配方设计.北京：化学工业出版社.1994,8.312-313。
[34]记奎江等.实用橡胶制品生产技术.北京：化学工业出版社.2001,3.322-327。
[35]杨清芝.现代橡胶工艺学.北京：中国石化出版社,1997.575-610。
[36]马大猷.现代声学理论基础.北京：科学出版社,2002.230～241。
[37]封维忠,蒋本浩.某型客车内饰材料吸声系数的测定.振动、测试与诊断.1994,14(4).54～58。
[2]李海涛,朱锡,石勇等.多孔吸声材料的研究进展.材料科学与工程学报.2004,22(6).934。
[3]吕玉恒.国内噪声控制近况评述.噪声与振动控制.2001,(6).14-17。
[4]马大猷主编.噪声控制学.北京：科学出版社,1987.232-302。
[5]胡俊明.吸声材料在改善建筑声环境质量中的作用和发展趋势.噪声与振动控制.1993,(3).2-4。
[6]张守梅,曾令可,黄其秀等.环保吸声材料的发展动态及展望.陶瓷学报.2002,23(1).56～61。
[7]Croker Malcolm J. Noise and Noise Control CRC Press Ine.1982, (2). 21-22。
[8]胡俊民.发展吸声材料,提高环境质量.保温材料与节能技术.2002,(5).7-11。
[9]陈月辉.声学功能橡胶.特种橡胶制品.2004,(1).57-58。
[10]程桂萍,陈宏灯,何德坪等.多孔铝的声学性能.东南大学学报.1998,28(6)169-172。
[11]HJ Lee, S H Eom, Y K Song, S S Cho. [J]. Materials Science and Technology. 2003,19(6).819-825.
[12]余欢,方立高,严青松.[J]. HotWorking Technology,2001, (1).36-39。
[12]汤慧萍,张正德.金属多孔材料的发展现状.稀有金属材料与工程.1997,26(1).1-6。
[13]金卓仁.泡沫金属吸声材料的研究.噪声与振动控制.1993,6(3).31-35。
[14]Andrews E W, Gibson L J. The influence of cracks, notches and holes on the tensile strength of cellular solids. Acta Materialia.2001,5,49. 2975-2979。
[15]Mccormack T M, Miller R, Kelser G, et al. Failure of sandwich beams with metallic foamcores. Int J Solids and Structures.2001,38.4901～4920。
[16]程桂萍,陈宏灯,何德坪,等.多孔铝在不同介质中的吸声性能.噪声与振动控制.1998,(5).29-34。
[17]赵增典,张勇,苗汇静.泡沫铝的吸声性能初探.兵器材料科学与工程.1998, 28(1).48-52。
[18]王月.孔结构对通孔泡沫铝水声吸声性能的影响.材料开发与应用.2001,(4)1624-1627。
[19]钱军民,李旭祥.聚合物岩棉发泡复合材料吸声性能的研究.材料开发与应用.2006,6,15(3).15-18。
[20]曾晓东,李旭祥,席莺等.聚氯乙烯-岩棉复合发泡吸声材料的研制.化工新型材料.1998,(5).37～42。
[21]洪宗辉主编.环境噪声控制工程.北京：高等教育出版社,2002.118-144。
[22]马保国,朱洪波,董荣珍.高效吸声材料的研制.新型建筑材料.2002,(5).42-43。
[23]周曦亚,凡波.吸声材料研究的进展.中国陶瓷.2004,10,40(5).26～27。
[24]刘伯伦,钟祥璋.提高多孔材料低频吸声性能的探讨.声学技术.1992,11.57-60。
[25]H. C. Strifors and GC. Gaunaurd. Wave propagation in isotropic lineary isoelastic media. J.Acoust.Soc.Am.1959,85.995～1004。
[26]P. C. Waterman and R.Truell. Multiple scattering of waves. J. Mach.Phy.1961,vol2. 512-537.
[27]G C. Gaunaurd and H. Uberall. Resonance theory of the effective properties of perforated solids. J. Acoust. Soc. Am.1982, vol71(2).282～295。
[28]G C. Gaunaurd and J. Barlow. Matrix viscosity and cavity-size distribution effective properties of perforated elastomers. J.Acoust.Soc.Am.1984, vol 75(1).23～34。
[29]R. L. Kliginan.,W. M. Madigosky and J. R. Barlow. Effective dynamic properties of composite viscoelastic materials. J. Acoust. Soc. Am.1982, vol 70(5).1437～ 1444。
[30]G C. Gaunaurd and W. Waterman. Comparison of effective medium theories for inhomogeous continua. J. Acoust. Soc. Am.1989,vol85(2).541～554。
[31]F.H.Kerr. The scattering of a plane elastic wave by spherical elasticinclusions. Int. J. Engng Sci.1992, vol30(2).169～186。
[32]赵光贤,任文坛.中国橡胶.2005,21(20).23-24。
[33]张殿荣,马占兴,杨清芝.现代橡胶配方设计.北京：化学工业出版社.1994,8.312-313。
[34]记奎江等.实用橡胶制品生产技术.北京：化学工业出版社.2001,3.322-327。
[35]杨清芝.现代橡胶工艺学.北京：中国石化出版社,1997.575-610。
[36]马大猷.现代声学理论基础.北京：科学出版社,2002.230～241。
[37]封维忠,蒋本浩.某型客车内饰材料吸声系数的测定.振动、测试与诊断.1994,14(4).54～58。