摘要
为了研究复合水泥材料固化铅污染土的强度特性,采用水泥、粉煤灰与脱硫石膏混合形成的固化剂(CFG)对铅污染土进行固化处理,基于正交试验的方法进行无侧限抗压强度测试,研究铅离子浓度与CFG掺量对土体强度特性的影响规律。结果表明:固化土的抗压强度随CFG掺量增加而增大,随铅离子浓度增加而降低;养护7 d前铅离子浓度和固化剂掺量对土体抗压强度的影响,前者大于后者,而7 d后后者大于前者;在3,7 d时2种因素对于土体的强度的影响均较小,在14 d时该影响大幅提升,到28 d时影响特别显著。结合试验成果,提出了基于养护龄期和CFG掺量的强度预测公式,研究成果可供从事铅污染土修复工作的科研人员参考。
Orthogonal unconfined compression test was conducted on lead-contaminated soil solidified by curing agent CFG(cement mixed with flyash and desulphurized gypsum) to investigate the strength characteristics of treated lead-contaminated soils varying with lead ion concentration and CFG dosage. Results reveal that the unconfined compressive strength of stabilized soils increases with the growth of CFG dosage, while reduces with the climbing of lead ion concentration. In the first seven days of curing, the effect of lead ion concentration is greater than that of curing agent dosage; after seven days, the influence of the dosage of curing agent is greater than that of lead ion concentration. At 3 d and 7 d of curing, the influences of both factors on soil strength are small, while at 14 d the influence greatly increases, and at 28 d, the effect is especially significant. Furthermore, the formula of strength prediction based on curing age and CFG dosage is proposed as a reference for the treatment of lead-contaminated soil.
引文
[1] GEELHOED J S, MEEUSSEN J C L, LUMSDON D G, et al. Modelling of Chromium Behaviour and Transport at Sites Contaminated with Chromite Ore Processing Residue: Implications for Remediation Methods[J]. Environmental Geochemistry & Health, 2001, 23(3):261-265.
[2] MEEGODA J N. Waste Immobilization Technologies[J]. Practice Periodical of Hazardous, Toxic & Radioactive Waste Management, 2009, 3(3):124-131.
[3] LEE D, WAITE T D, SWARBRICK G, et al. Comparison of Solidification/Stabilization Effects of Calcite Between Australian and South Korean Cements[J]. Cement & Concrete Research, 2005, 35(11):2143-2157.
[4] YIN C Y,SHAABAN M G,MAHMUD H B.Chemical Stabilization of Scrap Metal Yard Contaminated Soil Using Ordinary Portland Cement: Strength and Leachability Aspects[J]. Building & Environment, 2007, 42(2):794-802.
[5] 杜延军, 金飞, 刘松玉,等. 重金属工业污染场地固化/稳定处理研究进展[J]. 岩土力学, 2011, 32(1):116-124.
[6] 席永慧, 熊浩. 锌污染土固化处理实验研究[J]. 同济大学学报(自然科学版), 2012, 40(11):1608-1612.
[7] 查甫生, 刘晶晶, 许龙,等. 水泥固化重金属污染土干湿循环特性试验研究[J]. 岩土工程学报, 2013, 35(7):1246-1252.
[8] 魏明俐, 伍浩良, 杜延军,等. 冻融循环下含磷材料固化锌铅污染土的强度及溶出特性研究[J]. 岩土力学, 2015,36(增1):215-219.
[9] 张亭亭, 李江山, 王平,等. 磷酸镁水泥固化铅污染土的力学特性试验研究及微观机制[J].岩土力学, 2016,37(增2):279-286.
[10] 张亭亭,李江山,王平,等. 磷酸镁水泥固化铅污染土的应力-应变特性研究[J]. 岩土力学, 2016,37(增1):215-225.
[11] 刘玲, 刘海卿, 李喜林,等. 熟石灰-矿渣联合修复重金属污染土强度及淋滤特性研究[J]. 硅酸盐通报, 2016, 35(7):2065-2070.
[12] 林傲然,滕楠,崔文博,等. 固化重金属Pb污染土无侧限抗压强度增长规律的研究[J]. 路基工程, 2016, (4):133-137.
[13] 王贤昆, 庞建勇, 王强. 复合水泥土无侧限抗压强度正交试验研究[J]. 长江科学院院报, 2015, 32(12):72-75.
[14] 查甫生,许龙,崔可锐.水泥固化重金属污染土的强度特性试验研究[J]. 岩土力学, 2012, 33(3):652-656.
[15] 陈蕾, 刘松玉, 杜延军,等. 水泥固化含铅污染土无侧限抗压强度预测方法[J]. 东南大学学报(自然科学版), 2010, 40(3):609-613.