摘要
采用不同的激光束偏移量对Q235和SUS304两种薄钢板进行对接焊试验,利用光学显微镜、显微硬度仪和拉伸试验机研究了光束偏移量对焊接接头组织和性能的影响规律。结果表明:激光束偏向Q235侧时焊缝表面成形质量好,两侧金属均充分融化,熔池形貌较好;随着光束向SUS304侧移动,Q235侧热影响区组织中马氏体含量逐渐减少,铁素体含量增加且晶粒急剧长大;接头最大硬度出现在焊缝区,是Q235母材硬度的3. 5倍;接头平均抗拉强度可达300 MPa,且断裂位置均位于Q235母材处,偏移量为-0. 1 mm时,接头的综合拉伸性能最好。
The butt welding experiment of Q235 and SUS304 thin steel plates was carried out with different laser beam excursion,and the effect of beam migration on the microstructure and properties of welded joint was studied by optical microscope,microhardness tester and tensile testing machine. The results show that: when the laser beam is inclined to the side of Q235,the weld surface has good forming quality,the amount of metal melting on both sides is equal,and the weld pool morphology is good; As the beam moves towards SUS304,the martensite content in the heat affected area on the Q235 side gradually decreases,the ferrite content increases and the grains grow rapidly; The maximum hardness of the welding joint appears in the weld zone,and its hardness is 3. 5 times that of Q235 base metal; The average tensile strength of welded joints is up to 300 MPa,and the fracture positions are all located at the base material of Q235. When the offset is-0. 1 mm,the tensile strength and plasticity of welded joints are the best.
引文
[1]张侠洲,赵英建,王凤会,等. Q235B/304L复合板焊接接头组织与性能研究[J].焊接技术,2017,46(8):10-13.
[2] ZHANG Y,SUN D Q,GU X Y,et al. Nd/YAG pulsed laser welding of TC4 titanium alloy to 301L stainless steel via pure copper interlayer[J]. International Journal of Advanced Manufacturing Technology,2017,90:953-961.
[3] WANG Xue-dong,ZHANG Xiao-bing,ZHANG Xiao-peng,et al. Influence of Laser Pulse Energy and Pulse Duration on Change of States in Laser Hole Drilling[J]. Rare Metal Materials and Engineering,2013,42(S2):205-208.
[4] LEI Z L,DONG Z J,CHEN Y B. Microstructure and mechanical properties of laser welded Ti-22Al-27Nb/TC4 dissimilar alloys[J]. Materials Science&Engineering A,2013,559:909-919.
[5]高伟,阎启,黄坚.钢/铝异种金属激光填丝熔钎焊对接接头组织与性能分析[J].中国激光,2014(6):91-96.
[6]李晓靓,于治水,张培磊,等.激光熔-钎焊镀锌钢/铝异种金属的接头性能影响因素及改善措施[J].材料导报,2015(5):123-126.
[7]吴晓红.碳钢连续脉冲激光焊接工艺对比实验研究[J].应用激光,2014,31(1):57-61.
[8]黄永德,周兴汶,龙伟民,等.光束偏移量对DD407/GH1140激光焊接头性能的影响[J].稀有金属材料与工程,2018,47(5):1620-1624.
[9]宋志华,吴爱萍,姚为,等.光束偏移量对钛/铝异种合金激光焊接接头组织和性能的影响[J].焊接学报,2013,34(1):105-108.
[10]韦竺施,崔丽,贺定勇,等.钢/铝异种合金激光深熔焊接头界面金属间化合物的EBSD研究[J].材料工程,2018,46(7):113-120.
[11]李光福,李冠军,方可伟,等.异材焊接件A508/52M/316L在高温水环境中的应力腐蚀破裂[J].金属学报,2011,47(7):797-803.
[12]张子阳,王善林,柯黎明.束流偏移量对IC10/GH3039电子束焊接头成型及性能的影响[J].稀有金属,2018,42(8):826-831.
[13]张健,林仕君,苏绍兴,等.光纤激光焊接铝合金离焦量对焊缝成形的影响[J].激光与光电子学进展,2016(13):180-185.
[14]王文军,龚五堂. 304不锈钢激光焊接工艺及微观组织研究[J].应用激光,2018,38(2):245-249.
[15]张亦弛,赵占西,刘文,等.铝合金薄板Nd∶YAG脉冲激光焊焊接参数研究[J].热加工工艺,2016,45(9):219-226.