对10Ni5CrMoV钢及其接头疲劳裂纹扩展过程采用Paris模型进行拟合,并对参数c和m进行统计分析,结果表明,拟合得到的c和m与疲劳寿命吻合较好,lgc和m均符合正态分布,且具有良好的线性关系而疲劳裂纹扩展寿命呈成布尔分布。
Based on Paris' s model of fatigue crack propagation, a fiting formula for the course of fatigue crack growth of 10 Ni5 CrMoV steel and its welded joint was set up, and a statistical analysis on parameters c and m of the formula and fatigue crack growth life was carried out. The results showed that the parameters c and m were in good agreement with fatigue life data, the data of lg c and m complied with normal distribution and had great linear independence, and the fatigue crack growth life was a weibull distribution.
引文
[1] 陈孝渝. 潜艇和潜水器结构的低周疲劳[M]. 北京:国防工业出版社, 1990.
[2] 程靳, 赵树山. 断裂力学[M]. 北京:科学出版社, 2006.
[3] MCEVILY A J, BAO H, ISHIHARA S. A modified constitutive relation for fatigue crack growth[C]. Proceedings of the 7th International Fatigue Congrress(Fatigue’99),Beijing: Higher Education Press,1999:329—336.
[4] 崔维成. 金属疲劳裂纹扩展率曲线与S-N曲线之间的关系[J]. 船舶力学, 2002, 6(6):93—106.
[5] 程光旭, 楼志文, 匡震邦.焊接热影响区疲劳裂纹扩展的微观行为[J]. 焊接学报, 1992, 13(4):237—244.
[6] 盛骤, 谢式千, 潘承毅. 概率论与数理统计(第四版)[M]. 北京:高等教育出版社, 2008.