摘要
考察了凝胶-溶胶法制备二氧化钛的工艺参数,并在凝胶之前加入铁红或者铁黄,进行半导体复合,通过降解亚甲基蓝研究铁红和铁黄的加入对催化剂活性的影响。结果表明,铁红和铁黄与二氧化钛的复合提高了催化剂对有机物的降解率,铁红/二氧化钛复合半导体光催化剂的光催化性能更好,3h降解率达到了44.01%,高出基础实验10.07%。
The technological parameters of the preparation of titanium dioxide by gel-sol method were studied.And a semiconductor compound was made by adding iron red or iron yellow before the gel test.By degrading methylene blue,the effect of iron red and iron yellow on the activity of catalyst was studied.The results showed that the combination of iron red and iron yellow and titanium dioxide increased the degradation rate of the catalyst.Red iron/titanium dioxide composite semiconductor catalyst is better,degradation rate reached 44.01% after three hours and 10.07% higher than the base experiment.
引文
[1]郝红红.环境污水处理技术的应用与研究[J].绿色环保建材,2017(2):173.
[2]赵宝江,李江,王丽萍.污水处理厂节能减排的实现途径分析[J].环境保护与循环经济,2016(11):49-52.
[3]王洋,刘博,段武彪.纳米二氧化钛光催化材料研究进展[J].化学教育,2014(8):1-4.
[4]刘守新.光催化及光电催化基础与应用[M].北京:化学工业出版社,2006.
[5]罗志华,许可,孙理蓉,等.纳米TiO2薄膜的研究[J].上海有色金属,2007,28(1):36-42.
[6]马军委,张海波,董振波,等.纳米二氧化钛制备方法的研究进展[J].无机盐工业,2006,38(10):5-7.
[7]王洪梅,赵中一,陈莉莉.二氧化钛亲水性技术现状[J].环境与可持续发展,2003(2):36-39.
[8]黄徽.活性炭纤维负载二氧化钛光催化剂的制备、改性及性能研究[D].苏州:苏州大学,2007.
[9]胡素娟.二氧化钛/氧化铁光催化材料的制备及其性能研究[D].杭州:浙江工业大学,2012.
[10]张鹏.新型高效半导体光催化材料及光催化机理研究[D].天津:南开大学,2013.
[11]王俊鹏.半导体材料的能带调控及其光催化性能的研究[D].济南:山东大学,2013.
[12]郭澎湃,谢峰,曹伟,等.聚合凝胶法制备粉状纳米TiO2的影响因素[J].内江师范学院学报,2011,26(4):32-35.
[13]尹保忠.二氧化钛光催化剂的制备和改性研究[D].上海:华东师范大学,2004.
[14]方明.锐钛矿二氧化钛溶胶的制备、结构及性能[D].杭州:浙江大学,2006.
[15]廖东亮,肖新颜,张会平,等.溶胶-凝胶法制备纳米二氧化钛的工艺研究[J].化学工业与工程,2003,20(5):256-260.