双面结构电磁屏蔽材料的制备及性能研究
|
摘要
采用磁控溅射法在涤纶水刺非织造布单面和双面分别沉积了纳米结构的Cu薄膜,利用矢量网络分析仪对所制备样品的电磁屏蔽效能进行了测试,并理论计算分析了单面屏蔽材料和双面屏蔽材料的屏蔽效能。结果表明:在总镀膜时间相同的情况下,双面屏蔽材料的电磁屏蔽效能要明显优于普通单面屏蔽材料的电磁屏蔽效能;普通单面屏蔽材料只对低波有相对较好的屏蔽效果,而双面屏蔽材料对低波和高波都有相对较好的屏蔽效果,且随着电磁波频率的增大,其屏蔽效能呈增大的趋势。
Nanostructure copper film deposited on the one side and two sides of polyester fiber spunlace nonwovens by magnetron sputtering method.The electromagnetic shielding property of sample was tested by vector network analyzer.The shielding effectiveness of single shielding material and double shielding material were analyzed by theoretical calculation.Experimental results showed that the electromagnetic shielding property of double shielding material was obvious better than single shielding material on the same coating time.Single shielding material had better shielding effect to the low electromagnetic wave.However,double shielding material had better shielding effect to the low electromagnetic wave and high electromagnetic wave.The shielding effectiveness had the trend to increase with the increase of wave frequency.
Nanostructure copper film deposited on the one side and two sides of polyester fiber spunlace nonwovens by magnetron sputtering method.The electromagnetic shielding property of sample was tested by vector network analyzer.The shielding effectiveness of single shielding material and double shielding material were analyzed by theoretical calculation.Experimental results showed that the electromagnetic shielding property of double shielding material was obvious better than single shielding material on the same coating time.Single shielding material had better shielding effect to the low electromagnetic wave.However,double shielding material had better shielding effect to the low electromagnetic wave and high electromagnetic wave.The shielding effectiveness had the trend to increase with the increase of wave frequency.
引文
[1]葛安香,李凤艳,闫江山,等.金属化电磁屏蔽纺织品的研究现状[J].山东纺织科技,2015,56(2):37-40.
[2]刘琳,张东.电磁屏蔽材料的研究进展[J].功能材料,2015,46(3):3016-3022.
[3]陈先华,刘娟,张志华,等.电磁屏蔽金属材料的研究现状及发展趋势[J].兵器材料科学与工程,2012,35(5):96-100.
[4]张晓宁,毛倩瑾,王群.三明治型电磁屏蔽材料的制备与性能[J].材料研究学报,2002,16(5):536-540.
[5]张晓宁,王群,葛凯勇,等.合成纤维复合夹层屏蔽结构改性及其电磁特性研究[J].复合材料学报,2003,20(1):85-90.
[6]王锦成.电磁屏蔽材料的屏蔽原理及研究现状[J].化工新型材料,2002,30(7):16-18.
[7]陈省区.塑料机盒的抗EMI膜研究[D].杭州:浙江大学,2008.
[8]钟良,刘传慧,刘继胜,等.多层电磁屏蔽镀层制备工艺研究[J].工艺与检测,2008,11(4):82-83.
[9]张晓宁.层状复合电磁屏蔽材料的设计与制备[D].北京:北京工业大学,2000.
[10]蔡迎波,杨锋,佘亚军,等.三层电磁屏蔽复合材料结构设计[J].金属功能材料,2009,16(4):13-15,22.
[11]孟灵灵.涤纶基布表面磁控溅射纳米铜膜及性能研究[D].无锡:江南大学,2013.
[2]刘琳,张东.电磁屏蔽材料的研究进展[J].功能材料,2015,46(3):3016-3022.
[3]陈先华,刘娟,张志华,等.电磁屏蔽金属材料的研究现状及发展趋势[J].兵器材料科学与工程,2012,35(5):96-100.
[4]张晓宁,毛倩瑾,王群.三明治型电磁屏蔽材料的制备与性能[J].材料研究学报,2002,16(5):536-540.
[5]张晓宁,王群,葛凯勇,等.合成纤维复合夹层屏蔽结构改性及其电磁特性研究[J].复合材料学报,2003,20(1):85-90.
[6]王锦成.电磁屏蔽材料的屏蔽原理及研究现状[J].化工新型材料,2002,30(7):16-18.
[7]陈省区.塑料机盒的抗EMI膜研究[D].杭州:浙江大学,2008.
[8]钟良,刘传慧,刘继胜,等.多层电磁屏蔽镀层制备工艺研究[J].工艺与检测,2008,11(4):82-83.
[9]张晓宁.层状复合电磁屏蔽材料的设计与制备[D].北京:北京工业大学,2000.
[10]蔡迎波,杨锋,佘亚军,等.三层电磁屏蔽复合材料结构设计[J].金属功能材料,2009,16(4):13-15,22.
[11]孟灵灵.涤纶基布表面磁控溅射纳米铜膜及性能研究[D].无锡:江南大学,2013.