摘要
介绍了热浸镀铝工艺的研究进展。简述了镀层的结构,分析了镀层组织和性能的影响因素。对热浸镀铝未来的发展方向进行了展望。
The research progress of hot-dip aluminizing process was introduced. The coating structure was sketched. The influence factors for the microstructure and properties of the coating were analyzed. The prospects for the future development of hot dip aluminum were forecasted.
引文
[1]陈杰.表面预处理及镀后处理对连续热浸镀铝组织和性能的影响[D].西安:西安建筑科技大学,2017.
[2]李凌.钢铁表面热浸镀铝新工艺及镀层厚度控制模型研究[D].武汉:武汉理工大学,2005.
[3]宋世崐,刘顺华.钢材的连续热浸镀铝[J].金属热处理,2000(5):15-17.
[4]魏天斌.国外热镀铝钢带的发展趋势[J].武钢技术,1999,37(1):48-53.
[5]金哲.不同钢基体热浸渗铝层组织及循环氧化行为的研究[D].沈阳:东北大学,2014.
[6]李苏琴.钢材热浸镀铝新工艺[J].热处理,2001,16(4):20-22.
[7]王畅畅.钢材表面热浸镀铝技术研究进展[J].材料保护,2016,49(10):74-77.
[8] Heumann T, Dittrich N A.Structure character of the Fe2Al5intermetallics compound in hot dip aluminizing process[J].Metallk,1959(50):617-625.
[9]夏原,姚枚,李铁藩.热浸铝镀层的微观结构及形成机理[J].中国有色金属学报,1997(4):154-158.
[10] Cheng W J, Wang C J.Microstructural evolution of intermetallic layer in hot-dipped aluminide mild steel with silicon addition[J].Surface&Coatings Technology,2011,205(19):4726-4731.
[11] Yousaf M, Iqbal J, Ajmal M.Variables affecting growth and morphology of the intermetallic layer(Fe Al)[J].Materials Characterization,2011,62(5):517-525.
[12]孙伟,蔡启洲,罗强.RE对热浸镀铝镀层组织及耐腐蚀性能的影响[J].中国表面工程,2010,23(6):24-29.
[13]文九巴,胡鹏飞,李晓源.稀土铈对热浸渗铝钢耐高温氧化性能的影响[J].热处理,2005,20(1):18-21.
[14]佟桁,李文广,王峰,等.扩散退火温度对钢表面铁-铝金属化合物镀层的影响[J].电镀与涂饰,2015,34(16):909-913.
[15]孙伟,蔡启舟,罗强,等.扩散退火对热浸镀铝层组织与抗高温氧化性的影响[J].材料热处理学报,2011,32(1):114-120.
[16]范彬,文明才,廖建勇.扩散退火温度对热浸镀铝钢高温磨损性能的影响[J].热加工工艺,2016,45(4):212-216.
[17]李慧莉,李国喜,郑毅然,等.热浸镀铝钢的镀层结构分析[J].材料与冶金学报,2004,3(1):51-53.
[18]高峰,吴俊森.提抽过程中镀层厚度的模型推导及验证[J].金属制品,2000,26(4):6-10.