改性辐射松木材物理力学性能研究
|
摘要
研究了辐射松树脂浸渍材与热空气热处理树脂浸渍材、热压热处理树脂浸渍材的物理力学性能,为后续辐射松改性处理和加工利用提供参考。结果表明:相对于未处理材,浸渍处理提高了木材的密度、尺寸稳定性、力学性能;相对于浸渍材,热处理可进一步提高尺寸稳定性,但一定程度降低了力学强度。
The physical and mechanical properties of resin impregnated timber,hot air treatment of resin impregnated timber and heat pressure treatment of resin impregnated timber were studied,which could provide a reference for the modification,processing,and utilization of Radiata pine.The results showed that both impregnated and heat treated had an effect on physical and mechanical properties of wood.Compared with untreated wood,impregnation treatment could improve the density,dimensional stability and mechanical properties of wood;compared with resin,heat treatment could further improve the dimensional stability,but the mechanical strength was reduced to a certain extent.
The physical and mechanical properties of resin impregnated timber,hot air treatment of resin impregnated timber and heat pressure treatment of resin impregnated timber were studied,which could provide a reference for the modification,processing,and utilization of Radiata pine.The results showed that both impregnated and heat treated had an effect on physical and mechanical properties of wood.Compared with untreated wood,impregnation treatment could improve the density,dimensional stability and mechanical properties of wood;compared with resin,heat treatment could further improve the dimensional stability,but the mechanical strength was reduced to a certain extent.
引文
[1]魏金光,韦亚南,鲍敏振,等.辐射松重组木密度对其孔隙率和性能的影响[J].浙江农林大学学报,2018,35(3):519-523.
[2]顾炼百.木材改性技术发展现状及应用前景[J].木材工业,2012,26(3):1-6.
[3]尹江苹,郭娟,赵广杰,等.湿热-压缩处理木材的纤维素晶体结构变化[J].林产工业,2017,44(7):10-14.
[4]全鹏,李芸,牟玉姝,等.高温热处理对UF树脂改性杉木吸湿性和耐湿尺寸稳定性的影响[J].中南林业科技大学学报,2018,38(9):126-130.
[5]侯瑞光,李贤军,刘元,等.浸渍-热处理对杨木力学性能的影响[J].中南林业科技大学学报,2016,36(2):125-129.
[6]陈敏杰,张振伟,涂登云,等.热处理浸渍杨木性能研究[J].西北农林科技大学学报(自然科学版),2017,45(1):99-104,111.
[7]武国峰,姜亦飞,张浩,等.辐射松的化学改性及多层压缩干燥工艺[J].木材工业,2010,24(6):12-14.
[8]徐炜玥,朱愿,欧阳靓,等.聚乙二醇和高温热处理复合改性对杨木吸水性的影响[J].林业机械与木工设备,2012,40(2):23-26.
[9]高志强,张耀明,吴忠其,等.加压热处理对表层压缩杨木变形回弹的影响[J].木材工业,2017,31(2):24-28.
[10]GB/T 1933-2009木材密度测定方法[S].北京:中国标准出版社,2009.
[11]GB/T 1931-2009木材含水率测定方法[S].北京:中国标准出版社,2009.
[12]GB/T 1934.2-2009木材湿胀性测定方法[S].北京:中国标准出版社,2009.
[13]GB/T 1935-2009木材顺纹抗压强度试验方法[S].北京:中国标准出版社,2009.
[14]GB/T 1936.1-2009木材抗弯强度试验方法[S].北京:中国标准出版社,2009.
[15]GB/T 1936.2-2009木材抗弯弹性模量测定方法[S].北京:中国标准出版社,2009.
[16]GB/T 1941-2009木材硬度试验方法[S].北京:中国标准出版社,2009.
[17]LY/T 2490-2015改性木材尺寸稳定性测定方法[S].北京:中国标准出版社,2015.
[18]高文丽.热处理对速生杨木性能的影响研究[D].合肥:安徽农业大学,2014.
[19]侯瑞光.杨木浸渍增强-热处理特性研究[D].长沙:中南林业科技大学,2014.
[20]闫丽,党娅萍.热处理工艺对甘油/热处理木材性能的影响[J].西北林学院学报,2014,29(4):208-213.
[21]范敏,倪欧琪,俞珍权,等.热处理对东非黑黄檀物理力学性能的影响[J].南京林业大学学报(自然科学版),2014,38(2):31-35.
[22]全鹏,李芸,曹敏,等.高温热处理对UF树脂改性杉木力学强度的影响[J].中南林业科技大学学报,2017,37(12):153-158.
[23]孙龙祥.热处理工艺对樟子松性能影响的研究[D].北京:中国林业科学研究院,2014.
[24]王晓琴.脲醛树脂浸渍实木复合地板表板的性能研究[D].北京:北京林业大学,2010.
[25]杨燕,吕建雄,陈太安,等.真空高温热处理对思茅松木材化学成分和颜色的影响[J].林产工业,2016,43(4):32-36.
[26]魏立婷,杨松,韩淑伟,等.黄顶菊秸秆制备刨花板工艺研究[J].林业机械与木工设备,2017,45(9):24-27.
[27]封宇,刘文金.实木家具有机形结构设计研究[J].家具与室内装饰,2018(2):24-25.
[28]王秀芳,唐立华.针对木材纹理的木制品设计研究[J].家具与室内装饰,2017(3):22-23.
[29]刘建霞,李亚玲,王喜明,等.木材热压干燥过程中内部温度和水蒸气压力的变化规律[J].林产工业,2018,45(4):12-14,21.
[30]郝晓峰,熊新阳,李贤军,等.樟木过热蒸汽干燥工艺初探[J].林产工业,2018,45(9):58-62.
[31]梁善庆,罗建举.人工林米老排木材的物理力学性质[J].中南林业科技大学学报,2007,27(5):97-100,116.
[32]陈琳,徐伟,陈昌华,等.家具用速生杨木无机改性及其性能对比分析[J].家具,2018,39(2):7-10.
[33]于书贤,吴智慧,王雪花.实木家具常用硬阔叶材中高温热处理物理性能研究[J].家具,2018,39(2):28-30,35.
[34]潘泽华,吴燕,唐沁雯,等.纳米晶体与蓄光型发光材料复合改性水性聚氨酯木器涂层的物理力学性能研究[J].家具,2018,39(3):11-15.
[35]李坚.木材科学研究[M].北京:科学出版社,2009:6.
[2]顾炼百.木材改性技术发展现状及应用前景[J].木材工业,2012,26(3):1-6.
[3]尹江苹,郭娟,赵广杰,等.湿热-压缩处理木材的纤维素晶体结构变化[J].林产工业,2017,44(7):10-14.
[4]全鹏,李芸,牟玉姝,等.高温热处理对UF树脂改性杉木吸湿性和耐湿尺寸稳定性的影响[J].中南林业科技大学学报,2018,38(9):126-130.
[5]侯瑞光,李贤军,刘元,等.浸渍-热处理对杨木力学性能的影响[J].中南林业科技大学学报,2016,36(2):125-129.
[6]陈敏杰,张振伟,涂登云,等.热处理浸渍杨木性能研究[J].西北农林科技大学学报(自然科学版),2017,45(1):99-104,111.
[7]武国峰,姜亦飞,张浩,等.辐射松的化学改性及多层压缩干燥工艺[J].木材工业,2010,24(6):12-14.
[8]徐炜玥,朱愿,欧阳靓,等.聚乙二醇和高温热处理复合改性对杨木吸水性的影响[J].林业机械与木工设备,2012,40(2):23-26.
[9]高志强,张耀明,吴忠其,等.加压热处理对表层压缩杨木变形回弹的影响[J].木材工业,2017,31(2):24-28.
[10]GB/T 1933-2009木材密度测定方法[S].北京:中国标准出版社,2009.
[11]GB/T 1931-2009木材含水率测定方法[S].北京:中国标准出版社,2009.
[12]GB/T 1934.2-2009木材湿胀性测定方法[S].北京:中国标准出版社,2009.
[13]GB/T 1935-2009木材顺纹抗压强度试验方法[S].北京:中国标准出版社,2009.
[14]GB/T 1936.1-2009木材抗弯强度试验方法[S].北京:中国标准出版社,2009.
[15]GB/T 1936.2-2009木材抗弯弹性模量测定方法[S].北京:中国标准出版社,2009.
[16]GB/T 1941-2009木材硬度试验方法[S].北京:中国标准出版社,2009.
[17]LY/T 2490-2015改性木材尺寸稳定性测定方法[S].北京:中国标准出版社,2015.
[18]高文丽.热处理对速生杨木性能的影响研究[D].合肥:安徽农业大学,2014.
[19]侯瑞光.杨木浸渍增强-热处理特性研究[D].长沙:中南林业科技大学,2014.
[20]闫丽,党娅萍.热处理工艺对甘油/热处理木材性能的影响[J].西北林学院学报,2014,29(4):208-213.
[21]范敏,倪欧琪,俞珍权,等.热处理对东非黑黄檀物理力学性能的影响[J].南京林业大学学报(自然科学版),2014,38(2):31-35.
[22]全鹏,李芸,曹敏,等.高温热处理对UF树脂改性杉木力学强度的影响[J].中南林业科技大学学报,2017,37(12):153-158.
[23]孙龙祥.热处理工艺对樟子松性能影响的研究[D].北京:中国林业科学研究院,2014.
[24]王晓琴.脲醛树脂浸渍实木复合地板表板的性能研究[D].北京:北京林业大学,2010.
[25]杨燕,吕建雄,陈太安,等.真空高温热处理对思茅松木材化学成分和颜色的影响[J].林产工业,2016,43(4):32-36.
[26]魏立婷,杨松,韩淑伟,等.黄顶菊秸秆制备刨花板工艺研究[J].林业机械与木工设备,2017,45(9):24-27.
[27]封宇,刘文金.实木家具有机形结构设计研究[J].家具与室内装饰,2018(2):24-25.
[28]王秀芳,唐立华.针对木材纹理的木制品设计研究[J].家具与室内装饰,2017(3):22-23.
[29]刘建霞,李亚玲,王喜明,等.木材热压干燥过程中内部温度和水蒸气压力的变化规律[J].林产工业,2018,45(4):12-14,21.
[30]郝晓峰,熊新阳,李贤军,等.樟木过热蒸汽干燥工艺初探[J].林产工业,2018,45(9):58-62.
[31]梁善庆,罗建举.人工林米老排木材的物理力学性质[J].中南林业科技大学学报,2007,27(5):97-100,116.
[32]陈琳,徐伟,陈昌华,等.家具用速生杨木无机改性及其性能对比分析[J].家具,2018,39(2):7-10.
[33]于书贤,吴智慧,王雪花.实木家具常用硬阔叶材中高温热处理物理性能研究[J].家具,2018,39(2):28-30,35.
[34]潘泽华,吴燕,唐沁雯,等.纳米晶体与蓄光型发光材料复合改性水性聚氨酯木器涂层的物理力学性能研究[J].家具,2018,39(3):11-15.
[35]李坚.木材科学研究[M].北京:科学出版社,2009:6.