文摘
A method for fabricating high-efficiency Cu2ZnSn(S,Se)4 (CZTSSe) solar cells is presented, and it is based on a non-explosive, low-cost, and simple solution process followed by a two-step heat treatment. 2-Methoxyethanol was used as a solvent, and Cu, Zn, Sn, chloride salts, and thiourea were used as solutes. A CZTSSe absorber was prepared by sulfurising and then selenising an as-coated Cu2ZnSnS4 (CZTS) film. Sulfurisation in a sulfur vapour filled furnace for a long time (2 h) enhanced the crystallisation of the as-coated CZTS film and improved the stability of the CZTS precursor, and selenisation promoted further grain growth to yield a void-free CZTSSe film. Segregation of Cu and S at the grain boundaries, the absence of a fine-grain bottom layer, and the large grain size of the CZTSSe absorber were the main factors that enhanced the grain-to-grain transport of carriers and consequently the short-circuit current (Jsc) and efficiency. The efficiency of the CZTS solar cell was 5.0%, which increased to 10.1% after selenisation. For the 10.1% CZTSSe solar cell, the external quantum efficiency was approximately 80%, the open-circuit voltage was 450 mV, the short-circuit current was 36.5 mA/cm2, and the fill factor was 61.9%. Copyright