文摘
This paper presents investigations on the characterization of ductile damage and identification of the porosity-related material model parameters in a dual-phase steel DP600. As a modeling reference for the damage evolution, a variant from the Gurson model family is taken. The micromechanical investigations related to nucleation and growth of voids have been carried out. In order to show the void-volume evolution during the deformation, post-mortem scanning electron microscope (SEM) analysis of a notched tensile test is used. Using the ion beam slope cutting methodology to prepare the specimens for SEM analysis, the microstructure can be observed in 2D including the voids. In this way, for the dual-phase steel, characteristic damage behavior upon deformation due to interaction of martensite and ferrite can be investigated. The minimum void size (areal) that can be measured is 0.05 µm2. This resolution of the measurements provides the detection of the newly nucleated voids. For the related material parameters, void-size relevant criterion is applied to determine the newly nucleated voids at a certain plastic strain.