Objectives
The aim of this work was the preparation of a new fluoride-releasing dental material characterized by a release of fluoride relatively constant over time without any initial toxic burst effect. This type of delivery is obtained by a matrix controlled elution and elicits the beneficial effect of a low amount of fluoride on human dental pulp stem cells (hDPSCs) towards mature phenotype.
Methods
The modified hydrotalcite intercalated with fluoride ions (LDH-F), used as filler, was prepared via ion exchange procedure and characterized by X-ray diffraction and FT-IR spectroscopy. The LDH-F inorganic particles (0.7, 5, 10, 20 wt.%) were mixed with a photo-activated Bis-GMA/TEGDMA (45/55 wt/wt) matrix and novel visible-light cured composites were prepared. The dynamic thermo-mechanical properties were determined by dynamic mechanical analyzer. The release of fluoride ions in physiological solution was determined using a ionometer. Total DNA content was measured by a PicoGreen dsDNA quantification kit to assess the proliferation rate of hDPSCs. Alkaline phosphatase activity (ALP) was measured in presence of fluoride resins.
Results
Incorporation of even small mass fractions (e.g. 0.7 and 5 wt.%) of the fluoride LDH in Bis-GMA/TEGDMA dental resin significantly improved the mechanical properties of the pristine resin, in particular at 37 掳C. The observed reinforcement increases on increasing the filler concentration. The release of fluoride ions resulted very slow, lasting months. ALP activity gradually increased for 28 days in hDPSCs cell grown, demonstrating that low concentrations of fluoride contributed to the cell differentiation.
Conclusions
The prepared composites containing different amount of hydrotalcite filler showed improved mechanical properties, slow fluoride release and promoted hDPSCs cell proliferation and cell differentiation.