文摘
High-energy density Zinc-air batteries are currently of interest since they could play a key role in emerging large-scale energy storage applications. However, achieving good rechargeability of such metal-air batteries requires significant further research and development effort. Room Temperature Ionic liquids (RTILs) offer a number of ideal thermal and physical properties as potential electrolytes for large-scale energy storage applications and thus, can help increase the practicality of such electrochemical devices. This paper reports the synthesis and application of three novel quaternary alkoxy ammonium bis(trifluoromethylsulfonyl)amide based RTILs, with two or more ether functional groups designed to interact and solubilize zinc ions, in order to aid in the electrochemical reversibility of the metal. The anion is successfully reduced from, and re-oxidized into, the three alkoxy ammonium RTILs suggesting that they are potential candidates as electrolytes for use in zinc-air batteries. Cyclic voltammetry reveals that the presence of water reduces the activation barrier required to deposit zinc and assists stable charge/discharge cycling in an electrolyte consisting of 0.1 M Zn(NTf2)2 in the tri-alkoxy ammonium chain RTIL, [N2(20201)(20201)(20201)] [NTf2], with 2.5 wt.% H2O. Further experiments demonstrate that with such electrolyte a Zn electrode can complete at least 750 cycles at a current density of 0.1 mA/cm2 at room temperature.