Studying on tempering transformation and internal friction for low carbon bainitic steel

详细信息    查看全文

• 作者：Weijuan Li ; ^{liweijuan826@163.com" class="auth_mail" title="E-mail the corresponding author} ; Mingyu Cai ; Dong Wang ; Junwei Zhang ; Shengshi Zhao ; Peiying Shao
• 关键词：Low carbon bainite steel ; Tempering ; Carbide ; Yield strength ; Internal friction
• 刊名：Materials Science & Engineering A
• 出版年：2017
• 出版时间：2 January 2017
• 年：2017
• 卷：679
• 期：Complete
• 页码：410-416
• 全文大小：1727 K

文摘

The changes of microstructure during the process of tempering transformation were analyzed by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction and internal friction (IF) for low carbon bainite steel. The yield strength of the steel was tested after tempering transformation. The results showed that the microstructures of the experimental steel in rolled state were composed of lath bainite and granular bainite with a little Mo₂C and NbC precipitates. The lath width of bainite increased continuously with the tempering time. More cell structures with different orientations were formed in bainite laths. Furthermore, poly-gonization gradually began in some laths. The microstructure of granular bainite increased and was coarsened when it devoured the lath bainite continuously. The dislocation density of the bainitic ferrite decreased continuously as Mo₂C and NbC precipitations were further increasing. The peak value of Snoek decreased continuously in internal friction-temperature spectrum. The peak value of SKK at the surface decreased at first and then increased. The peak value of SKK at the center decreased firstly and then had little change. Besides, the yield strength of the steel increased firstly and then decreased.