Effect of grain size on the fatigue crack growth behavior of 2524-T3 aluminum alloy

详细信息    查看全文

• 作者：W.B. Shou^a ; D.Q. Yi^a ; ^b ; H.Q. Liu^a ; C. Tang^a ; F.H. Shen^a ; B. Wang^a ; ^b ; ^{wangbin325@263.net" class="auth_mail" title="E-mail the corresponding author}
• 关键词：Aluminum alloys ; Fatigue crack growth ; Crack closure ; Crack deflection ; Grain size
• 刊名：Archives of Civil and Mechanical Engineering
• 出版年：2016
• 出版时间：May 2016
• 年：2016
• 卷：16
• 期：3
• 页码：304-312
• 全文大小：2981 K

文摘

2524-T3 aluminum alloy sheets with different grain sizes (13 μm, 59 μm, 178 μm, 355 μm, 126 μm, and 87 μm) were prepared using methods such as rolling and annealing. The microstructures and mechanical properties of the 2524-T3 aluminum alloy sheets were studied using optical microscopy (OM), scanning electron microscopy (SEM), and tensile and fatigue crack growth (FCG) rate tests. The grain size had a significant effect on the fatigue crack growth (FCG) rate. Alloys with grain sizes between 50 and 100 μm exhibited high fatigue crack propagation resistances and the lowest FCG rates (da/dN = 1.05–1.45 × 10^−3 mm/cycle at ΔK = 30 MPa m^1/2). Microstructural observations revealed that fatigue cracks propagated more tortuously in the alloy with grain sizes within the range of 50–100 μm. This result is attributed to the combined effects of grain boundaries, crack deflection, fracture surface roughness-induced crack closure, and plasticity-induced crack closure.