To prepare interpenetrating alumina–copper composites, alumina foams were activated with titanium coating by chemical vapor deposition and then were infiltrated with molten copper by expendable casting process. The microstructure and phase composition of the composites were analyzed, and bending strength, electrical conductivity, friction and wear properties were tested. The results showed that the bonding between ceramic and metal was fine in the composites while no reactions took place between them because of the undissolved titanium coating. With increase of ceramic fraction, the electrical conductivity of the composite decreased, whereas the bending strength increased. The composite failure occurred by ductile fracture of the metal followed by fracture of the ceramic. The wear rate of the composites decreased with increase of ceramic fraction. And the wear of the composites was featured with ceramic struts peeling compared with ploughing and adhering wear for pure copper.