TiO2/TiC0.7N0.3 coatings were prepared by ball milling followed by oxidation.
class="label">•
In situ co-doping of C and N with simultaneous TiO2 formation was observed.
class="label">•
Improved photocatalytic activity under UV/visible light was noticed.
class="label">•
Synergism in co-doping and heterojunction formation promoted carrier separation.