Critical size bone defects raise great demands for efficient bone substitutes. Mimicking the
hierarchical porous architecture and specific biological cues of natural bone has been considered as an effective strategy to facilitate bone regeneration. Herein, a trimodal macro/micro/nano-porous scaffold loaded
with recombinant human bone morphogenetic protein-2 (rhBMP-2) was developed. With mesoporous bioactive glass (MBG) as matrix, a trimodal MBG scaffold (TMS)
with enhanced compressive strength (4.28 MPa,
porosity of 80%) was prepared by a “viscosity controlling” and “homogeneous particle reinforcing” multi-template process. A 7.5 nm, 3D cubic (
Im3
m) mesoporous structure was tailored for a “size-matched entrapment” of rhBMP-2 to achieve sustained release and preserved bioactivity. RhBMP-2-loaded TMS (TMS/rhBMP-2) induced excellent cell attachment, ingrowth and osteogenesis
in vitro. Further
in vivo ectopic bone formation and orthotopic rabbit radius critical size defect results indicated that compared to the rhBMP-2-loaded bimodal macro/micro- and macro/nano-porous
scaffolds, TMS/rhBMP-2 exhibited appealing bone regeneration capacity. Particularly, in critical size defect, complete bone reconstruction
with rapid medullary cavity reunion and sclerotin maturity was observed on TMS/rhBMP-2. On the basis of these results, TMS/rhBMP-2 developed here represents a promising bone substitute for clinical application and the concepts proposed in this study might provide new thoughts on development of future orthopedic biomaterials.
Statement of Significance
Limited self-regenerating capacity of human body makes the reconstruction of critical size bone defect a significant challenge. Current bone substitutes often exhibit undesirable therapeutic efficacy due to poor osteoconductivity or low osteoinductivity. Herein, TMS/rhBMP-2, an advanced mesoporous bioactive glass (MBG) scaffold with osteoconductive trimodal macro/micro/nano-porosity and osteoinductive rhBMP-2 delivery was developed. The preparative and mechanical problems of hierarchical MBG scaffold were solved without affecting its excellent biocompatibilities, and rhBMP-2 immobilization in sizematched mesopores was first explored. Combining structural and biological cues, TMS/rhBMP-2 achieved a complete regeneration with rapid medullary cavity reunion and sclerotin maturity in rabbit radius critical size defects. The design conceptions proposed in this study might provide new thoughts on development of future orthopedic biomaterials.