Branched TiO2 nanorod array was achieved via simple hydrothermal process. Au NPs decorated branched TiO2 array was prepared via photoreductioin method. The photocurrent density of Au/B-TiO2 reached to 2.5 mA/cm2 at 1.23 V vs RHE.