刊名:Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms
出版年:2016
出版时间:1 May 2016
年:2016
卷:374
期:Complete
页码:8-13
全文大小:1818 K
文摘
Iron phosphate glass (IPG) has gained recent interest for use in encapsulating radioactive waste for long term storage. In this work, we investigate 5 different compositions of iron phosphate glass. We consider amorphous structures of 3 known crystalline phases: Fe2+(P2O7)2, (P2O7)3 and Fe3+(PO3)3, and structures of IPG (40 mol% Fe2O3 and 60 mol% P2O5), with 4% and 17% Fe2+ ion concentrations.
Using constant volume molecular dynamics (MD), we quench a set of structures for each glass composition, to find the optimal density structure. We found that the lowest energy structures of IPG with 4% and 17% concentration of Fe2+, have a density of 3.25 and 3.28 g/cm3 respectively. This is slightly higher than the experimentally measured values of 2.9 and 2.95 g/cm3 respectively.
We also estimate an upper and lower bound on the melting temperatures of each glass, then for each glass, we simulate radiation damage cascades at 4 keV. The cascade structures can be in the form of either a concentrated thermal spike or more diffuse with sub-cascade branching. We found that the glass compositions with a higher Fe/P atomic ratio, contained a greater number of displacements after the cascade. We also found that the IPG with 4% Fe2+, contained slightly fewer displacements than the IPG with 17% Fe2+. This is consistent with our previous work, which showed that the threshold displacement energies are lower for glasses with a lower Fe2+ content. In all the simulations, many PO4 polyhedra are destroyed during the early stages of irradiation, but recover strongly over a time scale of picoseconds, leaving very few over or under co-ordinated P atoms at the end of the ballistic phase. This is in contrast to recent work in apatite. The strong recovery indicates that phosphate glasses with a low Fe2+ content could be good materials for waste encapsulation.
NGLC 2004-2010.National Geological Library of China All Rights Reserved.
Add:29 Xueyuan Rd,Haidian District,Beijing,PRC. Mail Add: 8324 mailbox 100083
For exchange or info please contact us via email.