文摘
Highly ordered TiO2 nanotube arrays have received great interest in the field of nanoscience and nanotechnology. In view of applications in devices, it is of paramount importance to control the growth over large areas. The results described in this paper show how the growth characteristics of anodic TiO2 oxide films can be tailored by controlling the orientation of the underlying substrate. The correlation between the growth characteristics of anodic, self-organized TiO2 nanotubes and the crystallographic orientation of the underlying titanium substrate grains has been studied using electron backscatter diffraction (EBSD), scanning electron microscopy (SEM), and micro-Raman spectrometry. The preferred formation site for self-organized, amorphous TiO2 nanotubes is Ti(111), whereas on Ti(001) grains no nanotube growth is observed. Instead, a compact oxide film is formed, exhibiting a mixed anatase and rutile nanocrystalline character with a large degree of structural disorder. As an intermediate case, on Ti(010) and on Ti(110) nanotubes form but are capped by a strongly chemically etched overlayer. It has been observed that TiO2 nanotubes exclusively form on grains with an orientation that allows for the formation of a thick valve metal oxide. This insight will enable controlled and effective growth over large areas of nanotubular films on titanium and presumably on other transition metals that did not show growth of nanotubular oxides before.