Characterization of high-alumina coal fly ash based silicate material and its adsorption performance to CO2
- 作者:Yinan Yan ; Yajun Gao ; Wenjing Tang ; Qiang Li…
- 关键词:Silicate Material ; High ; alumina Coal Fly Ash (HACFA) ; Carbon Dioxide (CO2) ; Adsorption ; Regeneration
- 刊名:Korean Journal of Chemical Engineering
- 出版年:2016
- 出版时间:April 2016
- 年:2016
- 卷:33
- 期:4
- 页码:1369-1379
- 全文大小:1,276 KB
- 参考文献:1.D. J. Hofmann, J. H. Butler and P. P. Tans, Atmos. Environ., 43, 2084 (2009).CrossRef
2.J. C. M. Pires, F. G. Martins, M. C. M. Alvim-Ferraz and M. Simões, Chem. Eng. Res. Des., 89, 1446 (2011).CrossRef 3.H. Li, J. P. Jakobsen, Ø. Wilhelmsen and J. Yan, Appl. Energy, 88, 3567 (2011).CrossRef 4.A. Nuchitprasittichai and S. Cremaschi, Int. J. Greenh. Gas Con., 13, 34 (2013).CrossRef 5.N. Hiyoshi, K. Yogo and T. Yashima, Micropor. Mesopor. Mater., 84, 357 (2005).CrossRef 6.L. S. Tan, A. M. Shariff, K. K. Lau and M. A. Bustam, J. Ind. Eng. Chem., 18, 1874 (2012).CrossRef 7.J. K. Adewole, A. L. Ahmad, S. Ismail and C. P. Leo, Int. J. Greenh. Gas Con., 17, 46 (2013).CrossRef 8.D. Berstad, R. Anantharaman and P. Neksa, Int. J. Refrig., 36, 1403 (2013).CrossRef 9.J. N. Knudsen, J. N. Jensen, P. J. Vilhelmsen and O. Biede, Energy Procedia, 1, 783 (2009).CrossRef 10.R. Bounaceur, N. Lape, D. Roizard, C. Vallieres and E. Favre, Energy, 31, 2556 (2006).CrossRef 11.A. Hart and N. Gnanendran, Energy Procedia, 1, 697 (2009).CrossRef 12.B. ZareNezhad and N. Hosseinpour, Energy Convers. Manage., 50, 1491 (2009).CrossRef 13.V. P. Mulgundmath, R. A. Jones, F. H. Tezel and J. Thibault, Sep. Pur. Technol., 85, 17 (2012).CrossRef 14.S. Himeno, T. Komatsu and S. Fujita, J. Chem. Eng. Data, 50, 369 (2005).CrossRef 15.A. A. Olajire, Energy, 35, 2610 (2010).CrossRef 16.M. G. Plaza, C. Pevida, B. Arias, J. Fermoso, M. D. Casal and C. F. Martín, Fuel, 88, 2442 (2009).CrossRef 17.N. A. Rashidi, S. Yusup and B. H. Hameed, Energy, 61, 440 (2013).CrossRef 18.R. V. Siriwardane, M. S. Shen and E. P. Fisher, Energy Fuel, 19, 1153 (2005).CrossRef 19.I. Majchrzak-Kuceba and W. Nowak, Thermochim. Acta, 437, 67 (2005).CrossRef 20.C. Stewart and M. Hessami, Energy Convers. Manage., 46, 403 (2005).CrossRef 21.Z. T. Yao, M. S. Xia, P. K. Sarker and T. Chen, Fuel, 120, 74 (2014).CrossRef 22.M. Ilic, C. Cheeseman, C. Sollars and J. Knight, Fuel, 82, 331 (2003).CrossRef 23.V. Manoharan, I. A. M. Yunusa, P. Loganathan, R. Lawrie, C. G. Skilbeck and M. D. Burchett, Fuel, 89, 3498 (2010).CrossRef 24.H. Lee, H. S. Ha, C. H. Lee, Y. B. Lee and P. J. Kim, Bioresour. Technol., 97, 1490 (2006).CrossRef 25.M. Erol, S. Kucukbayrak and A. Ersoy-Mericboyu, Fuel, 87, 1334 (2008).CrossRef 26.M. Erol, S. Kucukbayrak and A. Ersoy-Mericboyu, J. Hazard. Mater., 153, 418 (2008).CrossRef 27.J. Fang, G. Qin, W. Wei and X. Zhao, Sep. Pur. Technol., 80, 585 (2011).CrossRef 28.D. Jain, C. Khatri and A. Rani, Fuel Process. Technol., 91, 1015 (2010).CrossRef 29.E. Saputra, S. Muhammad, H. Q. Sun, H. M. Anga, M. O. Tadéa and S. B. Wang, Catal Today, 190, 68 (2012).CrossRef 30.X. P. Xuan, C. T. Yue, S. Y. Li and Q. Yao, Fuel, 82, 575 (2003).CrossRef 31.S. B. Wang and H. W. Wu, J. Hazard Mater., 136, 482 (2006).CrossRef 32.Y. Li, F. Zhang and F. Xiu, Sci. Tot. Environ., 407, 5780 (2009).CrossRef 33.M. Niewiadomski, J. Hupka, R. Bokotko and J. D. Miller, Fuel, 78, 161 (1999).CrossRef 34.M. Chareonpanich, T. Namto, P. Kongkachuichay and J. Limtrakul, Fuel Process. Technol., 85, 1623 (2004).CrossRef 35.Z. T. Yao, Y. Ye and M. S. Xia, Environ. Prog. Sustain., 32, 790 (2013).CrossRef 36.D. Wu, B. Zhang, L. Yan, H. Kong and X. Wang, Int. J. Miner. Process., 80, 266 (2006).CrossRef 37.A. Hernandez-Exposito, J. M. Chimenos, A. I. Fernandez, O. Font, X. Querol, P. Coca and F. Garcia Pena, Chem. Eng. J., 118, 69 (2006).CrossRef 38.F. Arroyo Torralvo and C. Fernández-Pereira, Miner. Eng., 24, 35 (2011).CrossRef 39.A. Shemi, R. N. Mpana, S. Ndlovu, L. D. van Dyk, V. Sibanda and L. Seepe, Miner. Eng., 34, 30 (2012).CrossRef 40.S. Dinda, Sep. Pur. Technol., 109, 64 (2013).CrossRef 41.J. M. Sun, Z. J. Zhang, G. Chen, S. Y. Yan, Q. Z. Huo and L. C. Wu, The method of active calcium silicate in the produce process of Al2O3 using high-alumina fly ash. C N. Patent. CN102249253A (2011). 42.Z. J. Zhang, J. M. Sun, H. F. Cao, X. Y. Zhang, Y. W. Wang and Q. Yao, A synthetical method of calcium silicate powder using highalumina fly ash. CN. Patent. CN101591023 (2008). 43.R. R. Yadav, S. N. Mudliarb, A. Y. Shekh, A. B. Fulke, S. S. Devi, K. Krishnamurthi, A. Juwarkar and T. Chakrabarti, Process Biochem., 47, 585 (2012).CrossRef 44.Y. Mogami, S. Yamazaki, S. Matsuno, K. Matsui, Y. Noda and K. Takegoshi, Cement Concrete Res., 66, 115 (2014).CrossRef 45.Y. Q. Zhang, A. V. Radha and A. Navrotsky, Geochim. Cosmochim. Ac., 115, 92 (2013).CrossRef 46.P. Tien and L. K. Chau, Chem. Mat., 11, 2141 (1999).CrossRef 47.H. Zaitan, D. Bianchi, O. Achak and T. Chafik, J. Hazard. Mater., 153, 852 (2008).CrossRef 48.R. A. Nyquist, C. L. Putzig and R. O. Kagel, Anne Leugers M. Infrared spectra of inorganic compounds. Michigan: Academic Press (1971). 49.T. Tsoncheva, G. Issa, T. Blasco, M. Dimitrov, M. Popova and S. Hernadez, Appl. Catal. A: Gen., 453, 1 (2013).CrossRef 50.M. V. Kok, Energy Sources, 24, 907 (2005).CrossRef 51.F. Ayari, E. Srasra and M. Trabelsi-Ayadi, Desalination, 185, 391 (2005).CrossRef 52.M. Sevilla and A. B. Fuertes, J. Colloid Interface Sci., 366, 147 (2012).CrossRef 53.H. Ucun, Y. K. Bayhan and Y. Kaya, J. Hazard. Mater., 153, 52 (2008).CrossRef 54.T. Fan, Y. Liu, B. Feng, G. Zeng, C. Yang, M. Zhou, H. Zhou, Z. Tan and X. Wang, J. Hazard. Mater., 160, 655 (2008).CrossRef 55.S. M. Tuzen, O. D. Uluözlü and M. Soylak, Biochem. Chem. Eng. J., 37, 151 (2007).CrossRef 56.J. M. Borah, J. Sarma and S. Mahiuddin, Colloids Surf., A, 387, 50 (2011).CrossRef 57.R. Serna-Guerrero and A. Sayari, Chem. Eng. J., 161, 182 (2010).CrossRef 58.J. Baltrusaitis and V. H. Grassian, J. Phys. Chem. B, 109, 12227 (2005).CrossRef 59.A. Wahby, J. M. Ramos-Fernandez, M. Martinez-Escandell, A. Sepulveda-Escribano, J. Silvestre-Albero and F. Rodriguez-Reinoso, ChemSusChem, 3, 974 (2010).CrossRef 60.M. Sevilla, P. Valle-Vigón and A. B. Fuertes, Adv. Funct. Mater., 21, 2781 (2011).CrossRef 61.M. Sevilla and A. B. Fuertes, Energy Environ. Sci., 4, 1765 (2011).CrossRef
- 作者单位:Yinan Yan (1)
Yajun Gao (1) Wenjing Tang (1) Qiang Li (1) Jianbin Zhang (1)
1. College of Chemical Engineering, Inner Mongolia University of Technology, Huhhot, 010051, China
- 刊物类别:Chemistry and Materials Science
- 刊物主题:Chemistry
Industrial Chemistry and Chemical Engineering Catalysis Materials Science Biotechnology
- 出版者:Springer New York
- ISSN:1975-7220
文摘
Silicate material prepared from high-alumina coal fly ash (HACFA) was characterized by using XRD, SEM, FTIR spectroscopy, TGA-DSC, and elemental analysis. These spectral results show that the silicate material is mainly composed of eight elements—O, C, Si, Ca, Na, Mg, Al, and Fe, which exist as the formations of Ca2+, Na+, Mg2+, Al3+, Fe3+, SiO 3 2− , and COO 3 2− , and some adsorbed water and crystal water are determined in the silicate material. The material with surface area of 117.12m2/g shows a faveolate structure, and a pore size distribution of silicate material is calculated at 11.01 nm from the nitrogen desorption isotherm using the BJH model. When the material was used for CO2 adsorption at T=323.15 K and flow rate=95mL/min with 15.79% (vol) CO2, a dynamic adsorption capacity of CO2 on the surface of silicate material was found at 8.67mg/g and the adsorption values decreased weakly after seventeen recycling times. The investigation of dynamic adsorption behavior shows that the silicate material presents similar adsorption properties with commercial active carbon and stronger adsorption properties than commercial diatomite.
| |