The competitive adsorption characteristics of welan gum and superplasticizer in cement mortar

详细信息    查看全文

• 作者：Qinglin Zhao 赵青林 ; Yulin Zhang ; Ciqi Liu…
• 关键词：welan gum ; superplasticizer ; competitive adsorption ; properties
• 刊名：Journal of Wuhan University of Technology--Materials Science Edition
• 出版年：2016
• 出版时间：February 2016
• 年：2016
• 卷：31
• 期：1
• 页码：131-138
• 全文大小：2,226 KB
• 参考文献：[1]Ding Q J, Zhu Y X, Wang Y, et al. Effects of Molecular Structure of Polycarboxylate-type Superplasticizer on the Hydration Properties of C3S[J]. J. Wuhan Univ. Technol. Mater. Sci. Ed., 2012, 27(4): 768–772CrossRef
  [2]Song Y M, Guo C C, Qian J S, et al. Adsorption Mechanism of Polycarboxylate-Based Superplasticizer in CFBC Ash-Portland Cement Paste[J]. J. Wuhan Univ. Technol. -Mater. Sci. Ed., 2014, 29(5): 945–949CrossRef
  [3]Kang K S, Veeder T V. Heteropolysaccharide S-130[P]. US Patent, US 4342866, 1982
  [4]Zhang Y, Zhang G P. Method for Preparing a Welan Gum[P]. Chinese Patent, CN200610012511.0, 2006
  [5]León-Martínez F M, Cano-Barrita P F de J, Lagunez-Rivera L, et al. Study of Nopal Mucilage and Marine Brown Algae Extract as Viscosity-enhancing Admixtures for Cement Based Materials[J]. Constr. Build. Mater., 2014, 53:190–202CrossRef
  [6]Plank J, Lummer N R, Dugonjic-Bilic F. Competitive Adsorption Between an AMPS-Based Fluid Loss Polymer and Welan Gum Biopolymer in Oil Well Cement[J]. J. Appl. Polym. Sci., 2010, 116: 2 913–2 919
  [7]Sonebi M, Lachemi M, Hossain K M A. Optimisation of Rheological Parameters and Mechanical Properties of Superplasticised Cement Grouts Containing Metakaolin and Viscosity Modifying Admixture[J]. Constr. Build. Mater., 2013, 38: 126–138CrossRef
  [8]Lachemia M, Hossaina K M A, Lambros V, et al. Self-consolidating Concrete Incorporating New Viscosity Modifying Admixtures[J]. Cem. Concr. Res., 2004, 34: 917–926CrossRef
  [9]Zhao Q L, Li B X. Ecological Dry-mixed Mortar[M]. Beijing: Chemical Industry Press, 2012.
  [10]Allen F L, Best G H, Lindroth T A. Welan Gum in Cement Compositions[P]. US Patent, US 4963668 A, 1989
  [11]Taylor H F W. Cement Chemistry[M]. London: Thomas Telford, 1997
  [12]Ma L, Zhao Q L, Yao C K, et al. Impact of Welan Gum on Tricalcium Aluminate-gypsum Hydration[J]. Mater. Charact., 2012, 62: 88–95CrossRef
  [13]Yuan X H, Chen W, Yang M. Effect of Superplasticizers on the Early Age Hydration of Sulfoaluminate Cement[J]. J. Wuhan Univ. Technol.-Mater. Sci. Ed., 2014, 29(4): 757–762CrossRef
  [14]Yang S L, Wu Y H, Li G X. Review on the Effects of Superplasticizer on the Crystallization of the Ettringite[J]. Sichuan Build. Sci., 2012, 38(3): 237–241
  [15]Elsen J, Lens N, Aarre T, et al. Determination of the W/C Ratio of Hardened Cement Paste and Concrete Samples on Thin Sections Using Automated Image Analysis Techniques[J]. Cem. Concr. Res., 1995, 25: 827–834CrossRef
  [16]He T, Zhao Q L, Xu Q W, et al. Effect of Different Chemical Admixtures on Rheological Properties of Cement Based Grouting[J]. Chin. Ceram. Soc. Bull., 2010, 29(3): 728–733
  [17]Pöllmann H. Calcium Aluminate Cement -Raw Materials, Differences, Hydration, and Properties[A]. In: Broekmans MATM, Pöllmann H editors. Applied Mineralogy of Cement and Concrete. Reviews in Mineralogy and Geochemistry[C]. Chantilly Virginia/USA, 2012: 1–82
  [18]Prince W, Espagne M, Aitcin P C. Ettringite Formation: a Crucial Step in Cement Superplasticizer Compatibility[J]. Cem. Concr. Res., 2003, 33: 635–641CrossRef
  
• 作者单位：Qinglin Zhao 赵青林 (1) (2)
  Yulin Zhang (1) (2)
  Ciqi Liu (1) (2)
  Luping Zeng (1) (2)
  Shihua Chen (2)
  
  1. State Key Laboratory of Silicate Materials for Architecture, Wuhan University of Technology, Wuhan, 430070, China
  2. School of Materials Science and Engineering, Wuhan University of Technology, Wuhan, 430070, China
  
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Chemistry
  Materials Science
  Chinese Library of Science
  
• 出版者：Wuhan University, co-published with Springer
• ISSN：1993-0437

文摘

Welan gum has been widely used in oil cement and grouting materials for its excellent rheological properties and anti-bleeding, and most of all, being friendly to the environment. However, when welan gum was added, the fluidity of mortar decreased sharply, so it should be used together with a superplasticizer to enable good workability. With its powerful charge density in the molecular structure, the competitive adsorption between welan gum and other admixtures happened remarkably during the addition process. Consequently, we experimentally studied on the bleeding rate and rheological properties of cement slurry, fluidity and mechanical properties of mortar with welan gum mixed with superplasticizer, aiming at understanding the competitive adsorption phenomenon by application of welan gum mixed with superplasticizer. By measuring the hydration heat and zeta potential, the mechanism of interaction of welan gum with superplasticizer was deduced and explained. The results showed that it could ensure a good dispersion effect when welan gum is mixed with the two kinds of superplasticizer. Welan gum had little impact on the naphthalene superplasticizer, but did have a substantial influence on polycarboxylate. In practice, adding welan gum after PCE acted with cement for 2 min could effectively avoid the competitive adsorption and then achieve better performance. On this viewpoint for mortar with PCE, new delay release welan gum needs further research and development. Key words welan gum superplasticizer competitive adsorption properties