Relaxation process in chitosan–oxalic acid solid polymer electrolytes
- 作者:I. A. Fadzallah (1)
S. R. Majid (1) M. A. Careem (1) A. K. Arof (1)
- 关键词:Chitosan ; Oxalic acid ; Ionic conductivity ; Electrical modulus
- 刊名:Ionics
- 出版年:2014
- 出版时间:July 2014
- 年:2014
- 卷:20
- 期:7
- 页码:969-975
- 全文大小:
- 参考文献:1. Ravi Kumar MNV (2000) React Funct Polym 46:1-7 CrossRef
2. Mukoma P, Jooste BR, Vosloo HCMJ (2004) J Power Sources 136:16-3 CrossRef 3. Smitha B, Anjali Devi D, Sridhar S (2008) Int J Hydrog Energy 33:4138-146 CrossRef 4. Ng LS, Mohamad AA (2008) J Membr Sci 325:653-57 CrossRef 5. Arof AK, Osman Z, Morni NM, Kamarulzaman N, Ibrahim ZA, Muhamad MR (2001) J Membr Sci 36:791-83 6. Boroglu MS, Celik SU, Bozkurt A, Boz I (2011) J Membr Sci 375:157-64 CrossRef 7. Goktepe F, Celik SU, Bozkurt A (2008) J Non-Cryst Solids 354:3637-642 CrossRef 8. Mohamed NS, Subban RHY, Arof AK (1995) J Power Sources 56:153-56 CrossRef 9. Morni NM, Arof AK (1999) J Power Sources 77:42-8 CrossRef 10. Morni NM, Mohamed NS, Arof AK (1997) Mater Sci Eng B 45:140-46 CrossRef 11. Subban RHY, Arof AK, Radhakrishna S (1996) Mater Sci Eng B 38:156 CrossRef 12. Ng LS, Mohamad AA (2006) J Power Sources 163:382-85 CrossRef 13. Tangaris GM, Psarras GC, Kouloumbi N (1998) J Mater Sci 33:2027-037 CrossRef 14. Woo HJ, Majid SR, Arof AK (2012) Mater Chem Phys 134:755-61 CrossRef 15. Belattar J, Achour ME, Brosseau C (2011) J Appl Phys 110(054101):1- 16. Cosgun S, Celik SU, Baykal A, Bozkurt A (2010) Curr Appl Phys 10:133-37 CrossRef 17. Dziaugys A, Banys J, Samulionis V, Vysochanskii Y (2008) Ultragarsas 63:7-0 18. Greicius S, Banys J, Szafraniak-Wiza I (2009) Process Appl Ceram 3:85-7 CrossRef 19. Diaz Calleja R, Matveeva ES, Parkhutik VP (1995) J Non-Cryst Solids 180:260-65 CrossRef 20. Ai L, Jiang J, Li L (2010) J Mater Sci 21:206-10 21. Dasari MP, Sambasiva Rao K, Krishna PM, Krishna GG (2011) Acta Phys Pol A 119:387-94 22. Mohomed K, Gerasimov TG, Moussy F, Harmon JP (2005) Polymer 46:3847-855 CrossRef 23. El-Nahass MM, Farid AM, Abd El-Rahman KF, Ali HAM (2008) Phys B 403:2331-337 CrossRef 24. Choi B-K, Kim Y-W (2004) Electrochim Acta 49:2307-313 CrossRef 25. Cheruku R, Govindaraj LG (2012) Mater Sci Eng B 177:771-79 CrossRef 26. Lopes AC, Costa CM, Sabater i Serra R, Neves IC, Gomez Ribelles JL, Lanceros-Mendez S (2013) Solid State Ionics 235:42-0 CrossRef 27. Pradhan DK, Choudhary RNP, Samataray BK (2008) Express Polym Lett 2:630-38 CrossRef 28. Psarras GC, Gatos KG, Karahaliou PK, Georga SN, Krontiras CA, Karger-Kocsis J (2007) Express Polym Lett 1:837-45 CrossRef 29. Pissis P, Kyritsis A (1997) Solid State Ionics 97:105-13 CrossRef 30. Krishnakumar V, Shanmugam G (2012) Ionics 18:403-11 CrossRef 31. Ayesh AS (2009) Polym J 41:616-21 CrossRef 32. Ambrus JH, Moynihan CT, Macedo CB (1972) J Phys Chem 76:32873295 33. Money BK, Hariharan K, Swenson J (2012) J Phys Chem B 116:7762-770 CrossRef
- 作者单位:I. A. Fadzallah (1)
S. R. Majid (1) M. A. Careem (1) A. K. Arof (1)
1. Centre for Ionics of University of Malaya (CIUM), Department of Physics, Faculty of Science, University of Malaya, Kuala Lumpur, 50603, Malaysia
- ISSN:1862-0760
文摘
We investigate the room temperature frequency dependence of electrical modulus for the polymer electrolytes consisting of chitosan and oxalic acid in the frequency range from 50?Hz to 1?MHz. Oxalic acid serves as the proton provider. It is found that the lowest imaginary electrical modulus is shown by the highest conducting sample OA40, which contains 60?wt.% chitosan and 40?wt.% oxalic acid. The electrical moduli for OA40 sample membrane at different temperatures are also studied, and the peak of the imaginary electrical modulus has been observed to shift towards higher frequency with increasing temperature. This indicates that relaxation is thermally assisted. Analysis of electrical modulus shows that the main relaxation process in chitosan–oxalic acid polymer electrolyte system is a non-Debye process associated with viscoelastic relaxation.
| |