文摘
This study evaluated the effect of tooth bleaching on the microtensile bond strength (¦ÌTBS) of an experimental primer to enamel. Materials used were an experimental tooth manicure system (Shofu) composed of primer and light-cured flowable resin composite. Flattened enamel surfaces of bovine teeth were bleached with Nite White Excel (Discus Dental) or Hi-Lite (Shofu), with nonbleached teeth used as a control group. Each bleaching group was subdivided into three bonding modes. These were group A, application of primer for 3 s, followed by 5 s of air blowing; group B, application of primer for 10 s, followed by 5 s of air blowing; and group C, application of 20 % phosphoric acid for 10 s, spraying with water for 5 s, and then air blowing for 5 s. The flowable resin paste was placed and polymerized after each enamel surface treatment. Using a low-speed diamond saw, the specimens were sectioned into beam-shaped samples with a cross-sectional area of approximately 1 mm2 at the bonded interface. The samples were subjected to the ¦ÌTBS test with a 1.0 mm/min crosshead speed. Data were statistically analyzed using two-way analysis of variance (ANOVA) followed by the Bonferroni/Dunn post-hoc test. The two-way ANOVA revealed significant differences in the effects of the bleaching systems and bonding mode, and significant differences were also found for the interaction between them (P < 0.01). There were no statistically significant differences in ¦ÌTBS values among the specimens in groups A and B regardless of bleaching or nonbleaching (P > 0.05). In contrast, the ¦ÌTBS value of group C without bleaching was significantly higher than that of all other experimental groups (P < 0.01).