Synthesis and characterization of permalloy-reinforced Al2O3 nanocomposite powders by mechanical alloying

详细信息    查看全文

• 作者：H. Beygi (1)
  S. A. Sajjadi (1)
  M. Zare (1)
  
• 关键词：Nanocomposite powders ; FeNi intermetallic ; Mechanical alloying ; Characterization
• 刊名：The International Journal of Advanced Manufacturing Technology
• 出版年：2014
• 出版时间：February 2014
• 年：2014
• 卷：70
• 期：9-12
• 页码：1653-1659
• 全文大小：688 KB
• 作者单位：H. Beygi (1)
  S. A. Sajjadi (1)
  M. Zare (1)
  
  1. Department of Materials Science and Metallurgical Engineering, Engineering Faculty, Ferdowsi University of Mashhad, Mashhad, Iran
  
• ISSN：1433-3015

文摘

Intermetallics of Fe and Ni, which are known as permalloy, are under attention due to their excellent magnetic performance. Besides, mechanical properties of the materials can be improved by decreasing crystallite size of FeNi intermetallics or by reinforcing them with hard secondary phases such as Al2O3. In this study, FeNi–Al2O3 nanocomposite powders with three different compositions were successfully synthesized through mechanical alloying of Fe2O3, Ni, and Al powders mixture. Characterization of the samples was accomplished by scanning electron microscopy, transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy and X-ray diffraction. Effects of various parameters such as chemical composition of received materials, milling time, and annealing on the phase evolution, morphology, and microhardness of samples were investigated. It was found that by the addition of Fe as diluent, the required milling time for formation of FeNi intermetallic increased. By increasing milling time, mean crystallite size of FeNi decreased and reach to about 28?nm for FeNi-30?wt% Al2O3 nanocomposite powder sample. TEM observations also showed that in situ-formed Al2O3 particles, with particle size of about 65?nm, were uniformly dispersed within FeNi matrix.