Low-Temperature Preparation of Superparamagnetic CoFe2O4 Microspheres with High Saturation Magnetization
- 作者:Hong Lei Yuan (1)
Yong Qiang Wang (1) Shao Min Zhou (1) Li Sheng Liu (1) Xi Liang Chen (1) Shi Yun Lou (1) Rui Jian Yuan (1) Yao Ming Hao (1) Ning Li (1)
- 关键词:Magnetism ; Nanostructure ; Superparamagnetism
- 刊名:Nanoscale Research Letters
- 出版年:2010
- 出版时间:November 2010
- 年:2010
- 卷:5
- 期:11
- 页码:1817-1821
- 全文大小:630KB
- 参考文献:1. A. Skumiel, J. Magn. Magn. Mater. 307, 85 (2006) CrossRef
2. S. Neveu, A. Bee, M. Robineau, D. Talbot, J. Colloid Interface Sci. 255, 293 (2002) CrossRef 3. H. Shi, Y. Duan, Nanoscale Res. Lett. 4, 480 (2009) CrossRef 4. J.H. Lee, Y.M. Huh, Y.W. Jun, J.W. Seo, J.T. Jang, H.T. Song, S. Kim, E.J. Cho, H.G. Yoon, J.S. Suh, Nat. Med. 13, 95 (2007) CrossRef 5. M.F. Casula, P. Floris, C. Innocenti, A. Lascialfari, M. Marinone, M. Corti, R.A. Sperling, W.J. Parak, C. Sangregorio, Chem. Mater. 22, 1739 (2010) CrossRef 6. S. Cao, Y.J. Zhu, M.Y. Ma, L. Li, L. Zhang, J. Phys. Chem. C 112, 1851 (2008) CrossRef 7. J. Xie, S. Peng, N. Brower, N. Pourmand, S.X. Wang, S.H. Sun, Pure Appl. Chem. 78, 1003 (2006) CrossRef 8. S. Ghosh, S. GhoshMitra, T. Cai, D.R. Diercks, N.C. Mills, D.L. Hynds, Nanoscale Res. Lett. 5, 195 (2010) CrossRef 9. C. Liu, B. Zou, A.J. Rondinone, Z.J. Zhang, J. Am. Chem. Soc. 122, 6263 (2000) CrossRef 10. E. Choi, Y. Ahn, S. Kim, D. An, K. Kang, B. Lee, K. Baek, H. Oak, J. Magn. Magn. Mater. 262, L198 (2003) CrossRef 11. S. Sun, H. Zeng, D. Robinson, S. Raoux, P. Rice, S. Wang, G. Li, J. Am. Chem. Soc. 126, 273 (2004) CrossRef 12. Y. Lee, J. Lee, C. Bae, J. Park, H. Noh, J. Park, T. Hyeon, Adv. Funct. Mater. 15, 503 (2005) CrossRef 13. W. Wu, Q.G. He, C.Z. Jiang, Nanoscale Res. Lett. 3, 397 (2008) CrossRef 14. R.J. Tackett, A.W. Bhuiya, C.E. Botez, Nanotechnology 20, 445705 (2009) CrossRef 15. T. Neuberger, B. Schopf, H. Hofmann, M. Hofmann, B. von Rechenberg, J. Magn. Magn. Mater. 293, 483 (2005) CrossRef 16. S.H. Xuan, Y.J. Wang, J.C. Yu, K.C. Leung, Chem. Mater. 21, 5079 (2008) CrossRef 17. P. Granitzer, K. Rumpf, A. Roca, M. Morales, P. Poelt, M. Albu, Nanoscale Res. Lett. 5, 374 (2010) CrossRef 18. K. Lee, S. Kim, D. Kang, J. Lee, Y. Lee, W. Kim, D. Cho, H. Lim, J. Kim, N. Hur, Chem. Mater. 20, 6738 (2008) CrossRef 19. N.Z. Bao, L.M. Shen, Y.A. Wang, J.X. Ma, D. Mazumdar, A. Gupta, J. Am. Chem. Soc. 131, 12900 (2009) CrossRef 20. Y. Wei, L. Li, X. Yang, G. Pan, G. Yan, X. Yu, Nanoscale Res. Lett. 5, 433 (2010) CrossRef 21. Z.P. Liu, S. Li, Y. Yang, Z.K. Hu, S. Peng, J.B. Liang, Y.T. Qian, New J. Chem. 27, 1748 (2003) CrossRef 22. W. Yu, H.Q. Xie, L.F. Chen, Y. Li, C. Zhang, Nanoscale Res. Lett. 4, 465 (2009) CrossRef 23. Y.H. Zheng, Y. Cheng, Y.S. Wang, L.H. Zhou, F. Bao, C. Jia, J. Phys. Chem. B 110, 8284 (2006) CrossRef 24. H.M. Yang, J. Ouyang, A.D. Tang, J. Phys. Chem. B 111, 8006 (2007) CrossRef 25. L.J. Zhao, H.J. Zhang, Y. Xing, S.Y. Song, S.Y. Yu, W.D. Shi, X.M. Guo, J.H. Yang, Y.Q. Lei, F. Cao, Chem. Mater. 20, 198 (2008) CrossRef 26. M. Rajendran, R.C. Pullar, A.K. Bhattacharya, D. Das, S.N. Chintalapudi, C.K. Majumdar, J. Magn. Magn. Mater. 232, 71 (2001) CrossRef 27. Z.J. Gu, X. Xiang, G.L. Fan, F. Li, J. Phys. Chem. C 112, 18459 (2008)
- 作者单位:Hong Lei Yuan (1)
Yong Qiang Wang (1) Shao Min Zhou (1) Li Sheng Liu (1) Xi Liang Chen (1) Shi Yun Lou (1) Rui Jian Yuan (1) Yao Ming Hao (1) Ning Li (1)
1. Key Lab for Special Functional Materials of Ministry of Education, Henan University, 475004, Kaifeng, People’s Republic of China
- ISSN:1556-276X
文摘
Based on a low-temperature route, monodispersed CoFe2O4 microspheres (MSs) were fabricated through aggregation of primary nanoparticles. The microstructural and magnetic characteristics of the as-prepared MSs were characterized by X-ray diffraction/photoelectron spectroscopy, scanning/transmitting electron microscopy, and vibrating sample magnetometer. The results indicate that the diameters of CoFe2O4 MSs with narrow size distribution can be tuned from over 200 to ~330?nm. Magnetic measurements reveal these MSs exhibit superparamagnetic behavior at room temperature with high saturation magnetization. Furthermore, the mechanism of formation of the monodispersed CoFe2O4 MSs was discussed on the basis of time-dependent experiments, in which hydrophilic PVP plays a crucial role.
| |