通过CMT(Cold Metal Transfer)冷金属过渡焊接的工艺对镁(AZ31B)-铝(6061)异种金属焊接性进行了研究,试验中选用AZ61,4043焊丝、采用热镀锌钢板HDG60作为过渡金属,分别用于镁-钢、铝-钢侧焊接,选取合适的焊接工艺参数,使其间接实现了镁-铝异种金属连接的目的。研究得出:使用这种方法可以形成镁-钢熔钎焊焊接接头,铝-钢熔钎焊焊接接头组成的复合接头;同时冷金属过渡焊接可以通过保持较低焊接热输入从而降低界面反应层的厚度;而且镀锌钢板中间过渡层的使用也避免了镁-铝直接焊接时形成的脆性金属间化合物,如Al_3Mg_2,Mg_(17)Al_(12)等。采用该方法连接的镁-铝异种金属焊接接头的抗拉强度超过180 MPa,并且有较好的断后伸长率,相比铝镁异种金属CMT直接焊接,性能得到很大的改善,因此使用镀锌钢板中间过渡层的使用实现铝镁异种金属之间的连接是一种行之有效的方法。
An investigation of dissimilar metal joining between AZ31 B Mg and 6061 Al by CMT( Cold Metal Transfer) welding was conducted. To achieve successful welding of Mg-Al dissimilar metals,hot-dip galvanized steelplate of HDG60 was selected as transition metal,AZ61 and 4043 welding wires were utilized in welding process of Mg-steel and Al-steel,respectively,and different welding parameters were used on each side. It is shown that the heat input is controlled effectively and the interface reaction layer is thin via CMT welding. The vacancy of brittle Al_3Mg_2 and Mg_17Al_12 intermetallic compounds during the direct welding of Mg to Al can be attributed to the appropriate selection of transition metal. The mechanical properties of the welded joint were optimized because MgZn,FeAl_3 and Fe_2Al_5 phases with smaller thickness are mainly formed on the welded joint interface. For example,the tensile strength is higher than 180 MPa and the elongation is good with regard to the CMT welded joint of Mg-Al dissimilar metals,which indicates that the Mg-Al dissimilar metal can be joined effectively by means of the transition metal.
引文
[1] Larsson J K. Overview of joining technologies in the automotive industry[J]. Welding Research Abroad,2003,49(6):29-45.
[2] Mohammadi J,Behnamian Y,Mostafsei A,et al. Friction stir welding joint of dissimilar materials between AZ31B magnesium and 6061 aluminum alloys:Microstructure studies and mechanical characterizations[J]. Materials Characterization,2015,101:189-207.
[3]雷祥,单际国,郑世卿.焊接工艺对6005A铝合金激光-MIG复合焊焊缝成形的影响[J].焊接,2008(7):25-32.
[4]帅朋,吴志生,赵菲,等.镁/铝异种材料焊接研究现状[J].焊接技术,2017,46(2):1-4.
[5]李慧.镁铝异种金属激光焊接的研究[D].北京:北京工业大学硕士学位论文,2007.
[6]魏强.镁铝异种材料点焊研究[D].南昌:南昌航空大学硕士学位论文,2012.
[7]任大鑫.镁合金及镁铝异种金属胶焊技术研究[D].辽宁大连:大连理工大学博士学位论文,2011.
[8]柳绪静,刘黎明,王恒,等.镁铝异种金属激光-TIG复合热源焊焊接性分析[J].焊接学报,2005,26(8):40-43.
[9]王快社,王训宏,沈洋,等. MB3镁合金与1060铝合金搅拌摩擦焊接研究[J].热加工工艺. 2005(9):29-31.
[10] Cao R,Wen B F,Chen J H,et al. Cold metal transfer joining of magnesium AZ31B-to-aluminum A6061-T6[J]. Materials Science and Engineering A:Structural Materials:Properties,Microstructure and Processing,2013,560:256-266.
[11] Cao R,Sun J H,Chen J H,et al. Weldability of CMT joining of AA6061T6 to boron steels with various coatings[J].Welding Journal,2014,93:193-204.