摘要
使用X射线衍射、电子背散射衍射、万能拉伸试验机等研究换向轧制对6016铝合金的组织和力学性能的影响,并与常规轧制工艺进行对比。结果表明:冷轧后普通轧制板材织构表现出典型的"唇式"冷轧织构特征,换向轧制弱化了强度的形变织构,β取向线织构密度降低,轧制态板材的屈服强度低于常规轧制板材;换向轧制板材组织含有较多等轴晶粒,且大小分布均匀;T4态换向轧制板材的强度、伸长率和r值高于普通轧制板材;Δr值低于普通轧制板材,表明换向轧制有效改善6016铝合金板材的成形性能。
The effects of alternative rolling on the microstructure and mechanical properties of 6016 aluminum alloy were studied by X-ray diffractometry,electron backscattered diffraction(EBSD)and tensile testing machine,and the alterative rolling results were compared with normal rolling. The results show that the texture of normal rolled sheet shows typical "lip type" cold rolling texture characteristics after cold rolling. The strong deformation textures are weakened and the texture density of β orientation line decreases through alternative rolling,and the yield strength is lower than that of normal rolled sheet. The structure of alternative rolled sheets contains more equiaxed grains,and the grain size distribution is uniform. The strength,elongation and r value of alternative rolled T4 state sheet are higher than those of normal rolled sheet,and the value Δr is lower than that of normal rolled sheet,which indicates that alternative rolling can effectively improve the formability of 6016 aluminum alloy sheet.
引文
[1]MCKENZIE P W J,LAPOVOK R. ECAP with back pressure for optimum strength and ductility in aluminum alloy 6016[J].Acta Materialia,2011,58(9):3212-3222.
[2]雷经发,许孟,刘涛,等.高应变率下6061铝合金力学性能及本构模型研究[J].兵器材料科学与工程,2019,42(1):74-78.
[3]刘星兴,唐建国,张新明,等.双级淬火对车身板用6016铝合金烤漆硬化效应的影响[J].中国有色金属学报,2014,24(5):1186-1193.
[4]谢锦岳. 6016铝合金板材的织构和微观组织研究[D].重庆:重庆大学,2015.
[5]GHOSH M,MIROUX A,KESTENS L A I. Correlating r-value and through thickness texture in Al-Mg-Si alloy sheets[J].Journal of Alloys and Compounds,2015,619:585-591.
[6]BARNWAL V K,RAGHAVAN R,TEBARI A,et al. Effect of microstructure and texture on forming behaviour of AA-6061 aluminium alloy sheet[J]. Materials Science&Engineering:A,2017,679:56-65.
[7]HAN J H,SUH J Y,JEE K K,et al. Evaluation of formability and planar anisotropy based on textures in aluminum alloys processed by a shear deforming process[J]. Materials Science and Engineering:A,2008,477(1/2):107-120.
[8]CHINO Y,HUANG Xinsheng,SUZUKI K,et al. Variation in texture and lankford value of 1070 aluminum sheet rolled by cone-shaped roll[J]. Journal of Materials Science&Technology,2013,29(2):175-179.
[9]凌利月,唐建国,刘文辉,等.蛇形轧制对Al-Mg-Si合金板材剪切变形及织构影响的模拟[J].中南大学学报(自然科学版),2017,48(9):2279-2287.
[10]SAITO Y,UTSUNOMIYA H,SUZUKI H,et al. Improvement in the r-value of aluminum strip by a continuous shear deformation process[J]. Scripta Materialia,2000,42(12):1139-1144.
[11]付垚,谢水生,熊柏青,等.铝合金蛇形轧制轧板曲率解析模型研究[J].稀有金属,2011,35(6):805-811.
[12]黄先明,王瑞琴,谢文龙,等. TA6钛合金板材换向轧制工艺研究[J].钛工业进展,2016,33(5):21-24.
[13]毛卫民,杨平,陈玲.材料织构分析原理与检测技术[M].北京:冶金工业出版社,2008:20-45.