摘要
文中依次采用溶胀褪色、剥色褪色和还原清洗褪色的方法,对分散染料染色的涤纶针织面料进行多重褪色研究。探讨了溶胀褪色、剥色褪色和还原清洗褪色处理条件对织物褪色率和强力保留率的影响。结果表明,二甲基亚砜溶胀褪色的最佳条件为浴比1∶16,温度120℃和时间30 min;N,N-二甲基甲酰胺剥色褪色的最佳条件为浴比1∶14,温度100℃和时间30 min;保险粉还原清洗剥色效果可以忽略不计。经二甲基亚砜溶胀褪色和N,N-二甲基甲酰胺剥色褪色处理后,褪色率高达97.8%,且断裂强力保留率为94.3%,符合涤纶针织面料褪色复染的要求。
This paper studied the multiple fading on polyester knitted fabrics dyed with disperse dyes by swelling, decolorization, and reduction washing to strip color. The influence of the treating conditions of swelling,decolorization, and reduction washing on the fading rate and strength retention rate was discussed. The results show that the optimum conditions for the dimethyl sulfoxide swelling are liquor ratio of 1∶16, temperature at 120 ℃, and time for 30 minutes. The optimum conditions for the N, N-dimethylformamide decolorization are liquor ratio of 1∶14,temperature at 100 ℃, and time for 30 minutes. The stripping effect of reduction washing of the sodium hydrosulfite is negligible. After treatment of the dimethyl sulfoxide swelling and N, N-dimethylformamide decolorization, the fading rate is up to 97.8%, and the breaking strength retention rate only reduces to 94.3%, which meet the repeating dyeing requirement of the polyester knitting fabric.
引文
[1]芦长椿.涤纶工业丝技术进展[J].合成纤维,2008,37(9):1-5.
[2]姚军义,王玉合,吴旭华,等.国内涤纶工业丝发展现状[J].合成技术及应用,2017,32(2):26-30.
[3]黄雪红.数码热升华直喷印花涤纶地毯的开发[J].针织工业,2017(10):37-39.
[4]陈维国,章俊玲,戴瑾瑾.高耐晒涤纶汽车内饰纺织品的染色加工[J].印染,2007,33(23):47-51.
[5]车用针织内饰产品设计综述[J].针织工业,2004(1):94-98.
[6]张阳,沈兰萍.涤纶汽车座椅面料阻燃工艺的优化[J].合成纤维,2015,44(7):40-42.
[7]张建春,石新辉.防护服热阻研究简介[J].中国个体防护装备,2000(3):36-39.
[8]王德诚.聚酯新原料回收再生技术[J].合成纤维工业,2006,29(2):46-49.
[9]郭凤芝,丛琳.涤纶针织面料服用性能测试及发展前景研究[J].针织工业,2006(11):46-50.
[10]吴宝宅,武志云,汪少朋,等.应用二甲基亚砜对废旧聚酯纺织品的脱色[J].纺织学报,2014,35(4):84-87.
[11]石娜,武志云,汪少朋,等.溶剂法回收废旧聚酯纺织品技术[J].纺织学报,2012,33(7):31-36.
[12]吴宝宅,武志云,汪少朋,等.DMF在聚酯纺织品脱色中的应用研究[J].染整技术,2013(6):11-14.