摘要
为研究格尔木盐渍土地区钢筋混凝土服役期间的退化过程,采用现场暴露的试验方法,对钢筋混凝土的退化过程进行跟踪研究.将相对动弹性模量评价参数、相对质量评价参数作为钢筋混凝土耐久性退化的2个因素,基于Weibull分布函数对其进行综合分析.结果表明,Weibull分布函数可以很好地对钢筋混凝土的退化过程进行表述;相对动弹性模量评价参数和相对质量评价参数可分别作为劣化前期和后期的评价指标;钢筋混凝土的失效时间为870 d.
To study the degenerative process during the time of reinforced concrete service in Golmud salinized soil area, the article made a follow-up investigation on the degenerative process of reinforced concrete with the test method of site-exposed. It comprehensively analyzed dynamic modulus of elasticity evaluation parameter and relative quality evaluation parameter based on the Weibull distribution function by taking both parameters as the 2 factors of reinforced concrete durability degradation. The result shows that, Weibull distribution function can well express the degenerative process of reinforced concrete; relative dynamic elastic modulus evaluation parameters and relative quality evaluation parameters can be taken as the evaluation index of earlier stage and latter stage of degradation respectively. The failure time of reinforced concrete is 870d.
引文
[1] 杨劲松.中国盐渍土研究的发展历程与展望[J].土壤学报,2008,45(5):837-845.
[2] 牛荻涛,石玉钗,雷怡生.混凝土碳化的概率模型及碳化可靠性分析[J].西安建筑科技大学学报:自然科学版,1995,39(3):252-256.
[3] 闫波,王幼青.大气污染对钢筋混凝土结构物耐久性影响研究[J].哈尔滨建筑大学学报,2000,33(3):39-43.
[4] 张誉,蒋利学.基于碳化机理的混凝土碳化深度实用数学模型[J].工业建筑,1998,28(1):16-19.
[5] 金伟良,张亮,鄢飞.函数型神经网络法在混凝土碳化分析中的应用[J].浙江大学学报:自然科学版,1998,32(5):519-525.
[6] MAAGE M,HELLAND S,POULSEN E.Service life prediction of exist-ing concrete structures exposed to marine environment[J].ACI Materials Journal,1996,93(6):602-608.
[7] 赵尚传,贡金鑫,水金锋.氯离子环境下既有钢筋混凝土桥梁耐久性的概率分析[J].公路交通科技,2006,23(7):82-86.
[8] 赵尚传.海洋环境中氯离子侵蚀与混凝土碳化诱发钢筋锈蚀失效概率的对比分析[J].公路,2008(4):163-165.
[9] 马亚丽,张爱林.基于规定可靠指标的混凝土结构氯离子侵蚀耐久寿命预测[J].土木工程学报,2006,39(2):36-41.
[10] 金伟良,张苑竹.预估混凝土氯离子分布的新方法[J].浙江大学学报:工学版,2004,38(2):195-199.
[11] 孙淑霞,李良巧,孙志礼,等.齿轮可靠度计算中随机因素影响程度的计算分析[J].机械传动,2008,32(3):80-82.
[12] KUNTMAN A,ARDALI A,KUNTMAN H,et al.A Weibull distribution-based new approach to represent hot carrier degradation in threshold voltage of MOS transistors[J].Solid-State Electronics,2004,48(2):217-223.
[13] 刘平,马履一,贾黎明,等.油松、侧柏人工林树冠率的Weibull分布及动态预测[J].福建林业科技,2008,35(3):19-26.
[14] 周嫄娜,李炜.碳纤维单丝强度WEIBULL分析与研究[J].高科技纤维与应用,2015,40(6):35-40.
[15] 何海杰.兰州地区现场暴露普通混凝土耐久性试验研究及寿命预测[D].兰州:兰州理工大学,2013.
[16] 乔宏霞.混凝土抗硫酸盐腐蚀耐久性的评价方法研究[D].兰州:兰州理工大学,2007.
[17] HINES W W,MONTGOMERY D C.Probability and Statistics in Engineering and Management Science[M].New York:John Wiley & Sons,1990.
[18] 雷刚.Weibull分布寿命数据的参数估计[D].武汉:华中科技大学,2006.